Purell RP378T
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Purell |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UF6ktG_Purell-RP378T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Purell RP378T is a polypropylene random copolymer with nucleation and antielectrostatic agent. It exhibits a very good flowability and a good transparency. Purell RP378T is used for injection moulding medical and pharmaceutical applications only after approval by LyondellBasell. For regulatory information please refer to Purell RP378T Product Stewardship Bulletin (PSB). Without exception, all potential activities for applications in the pharmaceutical, medical device, laboratory and diagnostics area have to be discussed with the relevant Technical (P & AD) and Business contacts first. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 48 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 65.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 58.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1150 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 29.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 11 | % | |
| Break | > 50 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| 0°C | 2.5 | kJ/m² | |
| 23°C | 4.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| 0°C | 60 | kJ/m² | |
| 23°C | 180 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 70.0 | °C | ASTM D648, ISO 75-2/B |
| Vicat Softening Temperature | |||
| -- | 130 | °C | ISO 306/A50 |
| -- | 72.0 | °C | ISO 306/B50 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (1000 µm, Injection Molded) | 7.0 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYNIL® P50 FI | Nilit Plastics | Nylon 66 | POLYNIL® |
| MOSTEN FT 005 | UNIPETROL RPA | PP Homopolymer | MOSTEN |
| HiFill® PA6 GF/M40 HS L | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| Hostacom ERC 198N | LyondellBasell Industries | PP Copolymer | Hostacom |
| ICORENE® 9402 | ICO Polymers EMEA, A Division of A. Schulman | TPE | ICORENE® |