Royalstat R67
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Spartech Plastics |
| Trademark: | Royalstat |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UEZ0lD_Royalstat-R67.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Royalstat R67 is an acrylonitrile butadiene styrene (ABS) product,. It can be processed by vacuum molding and is available in North America. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 98 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 27.6 | MPa | ASTM D638 |
| Flexural Modulus | 1720 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 44.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dart Drop Impact (3.18 mm) | 13.6 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 104 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 93.3 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+6 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+4 | ohms·cm | ASTM D257 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRIMMA® SD6350H | Samyang Corporation | Acrylic (PMMA) | TRIMMA® |
| AEI SX703:CM488-6 | AEI Compounds Limited | HDPE | AEI |
| Complet® LGF50-PA66 MT | PlastiComp, Inc. | Nylon 66 | Complet® |
| Hytrel® SC956 NC010 | DuPont Performance Polymers | TPC-ET | Hytrel® |
| Karina BLACK PVC COMPOUND -E 742-48/ 1-G-IS-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |