Hyrene® PS-HI 8/2
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Entec Polymers |
| Trademark: | Hyrene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UDToOl_Hyrene-PS-HI-8-2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hyrene® PS-HI 8/2 is a High Impact Polystyrene material. It is available in North America. Important attributes of Hyrene® PS-HI 8/2 are:
Typical application of Hyrene® PS-HI 8/2: Food Contact Applications |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 7.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C, Injection Molded) | 26.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C, Injection Molded) | 55 | % | ASTM D638 |
| Flexural Modulus (23°C, Injection Molded) | 1990 | MPa | ASTM D790 |
| Flexural Strength (23°C, Injection Molded) | 39.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 130 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 85.6 | °C | ASTM D648 |
| Vicat Softening Temperature | 100 | °C | ASTM D1525 1 |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ADDINYL C2 R | ADDIPLAST | Nylon 66/6 | ADDINYL |
| ALFATER XL® A55E 1GP0000 | ALBIS PLASTIC GmbH | TPV | ALFATER XL® |
| CERTENE™ SIM-120 | Muehlstein | PS (HIPS) | CERTENE™ |
| Epoxies, Ect. 60-7155 | Epoxies, Etc. | Epoxy | Epoxies, Ect. |
| Neoflex™ 8058 | Zylog Plastalloys Pvt. Ltd. | TPE | Neoflex™ |