| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UDKm7B_LNPTHERMOCOMPWF006Hcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP WF006H is a compound based on Polybutylene Terephalate resin containing Glass Fiber. Also known as: LNP* THERMOCOMP* Compound WF-1006 HC Product reorder name: WF006H |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.62 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (24 hr) | 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 10400 | MPa | ASTM D638 |
| Tensile Strength (Break) | 120 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.7 | % | ASTM D638 |
| Flexural Modulus | 9450 | MPa | ASTM D790 |
| Flexural Strength | 186 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 69 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 710 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 208 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® TL-1120E | Teknor Apex Company | TPE | Telcar® |
| Titanvene™ HD5002GA | PT. TITAN Petrokimia Nusantara | HDPE | Titanvene™ |
| Latamid 66 H-V0 | LATI S.p.A. | Nylon 66 | Latamid |
| LNP™ STAT-KON™ OE006C1 compound | SABIC Innovative Plastics | PPS, Linear | LNP™ STAT-KON™ |
| Sylvin 8820H-93 ORANGE 539 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |