Badamid® LB70 K
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Bada AG |
| Trademark: | Badamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UD7pin_Badamid-LB70-K.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Badamid® LB70 K is a Polyamide 6 (Nylon 6) material. It is available in Europe. Primary attribute of Badamid® LB70 K: Flame Rated. |
| General Information |
|---|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.13 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 9.0 to 10 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.6 to 3.4 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 3100 | 1000 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 85.0 | 40.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 4.5 | 20 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break (23°C) | 10 | > 50 | % | ISO 527-2/50 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 3.0 | -- | kJ/m² | |
| 23°C | 5.0 | 55 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 200 | -- | kJ/m² | |
| 23°C | 250 kJ/m² | No Break | ||
| Notched Izod Impact Strength (23°C) | 5.0 kJ/m² | No Break | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 180 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 65.0 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 1 | 220 | -- | °C | ISO 3146 |
| CLTE - Flow | 7.0E-5 to 1.0E-4 | -- | cm/cm/°C | DIN 53752 |
| Maximum Service Temperature | IEC 60216 | |||
| -- 2 | 100 | -- | °C | |
| -- | 180 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | 1.0E+10 | ohms·cm | IEC 60093 |
| Relative Permittivity (1 MHz) | 3.50 | 7.00 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.023 | 0.30 | IEC 60250 | |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | HB | -- | ||
| 1.60 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 10 K/min |
| 2 . | 20000 H |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer SV-16000U | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| Teflon® FEP TE-9568 | DuPont Fluoropolymers | FEP | Teflon® FEP |
| Sylvin 7833-65 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| AIE PPO 9010F-S085A | Asia International Enterprise (Hong Kong) Limited | PPE+PS | AIE PPO |
| HONES® PPS HS-5066A | Guangdong Shunde Hones Polymer Material Co., Ltd. | PPS | HONES® |