NEFTEKHIM ABS 0475E
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Nizhnekamskneftekhim Inc. |
| Trademark: | NEFTEKHIM ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UBfeZe_NEFTEKHIM-ABS-0475E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ABS 0475E- is a grade with high impact strength applied for sheet extrusion. It is a good processed grade with enhanced heat resistance intended for production of sheet extrusion (coextruded or not) for sanitary appliances and transport components. It is produced self-colored only, free of additives and dye. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 3.0 to 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.60 | % | |
| Water Absorption (Equilibrium) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 103 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 44.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 45 | % | ASTM D638 |
| Flexural Modulus | 2200 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 60.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 20 | kJ/m² | DIN 53453 |
| Notched Izod Impact Strength (23°C) | 20 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 100 | °C | ASTM D1525 1 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.17 | W/m/K | ASTM C177 |
| Deflection Temperature | 100 | °C | ASTM D648 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Residual Styrene 2 | 0.050 | % | Internal Method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Ignition Temperature | 650 | °C | IEC 60695-2-1 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60°) | 60 | ASTM D523 |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| 2 . | Test Method: TU 2214-159-05766801-2011 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Scolefin 52 G 13-9 | Ravago Group | PP Homopolymer | Scolefin |
| THERMOLAST® K TC7GPZ (Series: GP/FG) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Ultradur® S 4090 GX | BASF Corporation | PBT+ASA | Ultradur® |
| UMG ABS® FV700G4 | UMG ABS, Ltd. | ABS | UMG ABS® |
| LEXAN™ ML6411 resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |