RTP 2800-55A
| Category: | TPO (POE) , Thermoplastic Polyolefin Elastomer |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UB8HDW_RTP-2800-55A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.968 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | ASTM D955 | ||
| 3.18mm, injection molding | 1.8 | % | ASTM D955 |
| 6.35mm, injection molding | 2.5 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.050 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 55 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 70.0 | MPa | ASTM D638 |
| Flexural Modulus (Injection Molded) | 70.0 | MPa | ASTM D790 |
| Flexural Strength (Injection Molded) | 3.00 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 3.00 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 300 | % | ASTM D412 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm, Injection Molded) | No Break | ASTM D256 | |
| Unnotched Izod Impact (3.18 mm) | No Break | ASTM D4812 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Additional Information |
|---|
| The value listed as Flammibility, UL 94, was tested in accordance with RTP Company methods. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 171 - 199 | °C | |
| Middle Temperature | 171 - 199 | °C | |
| Front Temperature | 171 - 199 | °C | |
| Mold Temperature | 16.0 - 66.0 | °C | |
| Injection Pressure | 83.0 - 124 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1300 TC-I-20 SE | RTP Company | PPS | RTP |
| Pro-fax 6331 | LyondellBasell Industries | PP Homopolymer | Pro-fax |
| KumhoSunny PET HEG3630 | Shanghai KumhoSunny Plastics Co., Ltd. | PET | KumhoSunny PET |
| LNP™ KONDUIT™ PX09322 compound | SABIC Innovative Plastics Asia Pacific | Nylon 6 | LNP™ KONDUIT™ |
| Petlon R-Prime A2-00-00-BK | Petlon Polymers Ltd | Nylon 6 | Petlon R-Prime |