RTP 1400 N
| Category: | PESU , Polyethersulfone |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UA9nY0_RTP-1400-N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High Viscosity |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (385°C/2.16 kg) | 30 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.60 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.54 | % | ASTM D570 |
| Moisture Content | 0.040 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 127 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2690 | MPa | ASTM D638 |
| Tensile Strength | 82.7 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 6.5 | % | ASTM D638 |
| Flexural Modulus | 2900 | MPa | ASTM D790 |
| Flexural Strength | 111 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 85 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 204 | °C | ASTM D648 |
| CLTE - Flow | 4.9E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+12 | ohms·cm | ASTM D257 |
| Dielectric Strength 1(in Oil) | 15 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.50 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 5.6E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 6.0 | hr | |
| Dew Point | -31.7 | °C | |
| Processing (Melt) Temp | 343 - 377 | °C | |
| Mold Temperature | 135 - 177 | °C | |
| Injection Pressure | 68.9 - 103 | MPa |
| Injection instructions |
|---|
| Desiccant Type Dryer Required. |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4000 AFA-6145 V0 | RTP Company | PPA | RTP |
| Small Boss SPVC2002 | Tongxiang Small Boss Special Plastic Products Co., Ltd. | PVC, Flexible | Small Boss |
| TAIRIPRO K4038 | Formosa Plastics Corporation | PP Random Copolymer | TAIRIPRO |
| Moplen EP200S | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| Hostaform® UV90Z XAP2 ™ | Celanese Corporation | PPS | Hostaform® |