TECHNO ABS DN5534
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Techno Polymer America, Inc. |
| Trademark: | TECHNO ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | U9x8ti_TECHNO-ABS-DN5534.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (240°C/10.0 kg) | 7.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 47.0 | MPa | ISO 527-2 |
| Flexural Modulus | 2260 | MPa | ISO 178 |
| Flexural Stress | 71.0 | MPa | ISO 178 |
| Coefficient of Friction | 0.10 | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 14 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 89.0 | °C | ISO 75-2/B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 98.9 to 110 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Rear Temperature | 229 to 271 | °C | |
| Middle Temperature | 229 to 271 | °C | |
| Front Temperature | 229 to 271 | °C | |
| Mold Temperature | 100 to 160 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® FR22F-N | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| Endura® FR-6780 | PMC Group Polymer Products | PP Copolymer | EnDura® |
| Honeywell PCTFE P4000LS | Honeywell | PCTFE | Honeywell PCTFE |
| KumhoSunny PET HEG3615 | Shanghai KumhoSunny Plastics Co., Ltd. | PET | KumhoSunny PET |
| TECHNO MUH E1500 | Techno Polymer Co, Ltd. | ABS | TECHNO MUH |