POLYTROPE® STR 1032EU-01 NATURAL
| Category: | Polyolefin, Enhanced TPO , Enhanced TPO Polyolefin |
| Manufacturer: | A. Schulman Inc. |
| Trademark: | POLYTROPE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | U9IKYT_POLYTROPE-STR-1032EU-01-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| POLYTROPE STR 1032EU resin is a cost efficient, high melt strength thermoformable TPO material that provides an economical balance of impact resistance and stiffness similiar to ABS, but provides the benefits of dimensional stability, chemical and weathering resistance characteristic of TPO materials. It can be extruded in smooth or textured surfaces, or co-extruded with a POLYTROPE STR enhanced polyolefin cap resin to further customize its' durability, appearance, or feel for interior and exterior applications. The capability of POLYTROPE STR 1032EU to provide an exceptionally smooth surface in extrusion and thermoforming makes it well suited to lamination processes with decorative films. It is also easily colored and is paintable by standard TPO paint systems. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.13 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.70 | g/10 min | ISO 1133 |
| Molding Shrinkage (23°C, 24 hr, 3.18 mm) | 0.80 to 1.2 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 2(Yield, 23°C) | 23.0 | MPa | ISO 527-2 |
| Tensile Strain 3(Break, 233°C) | 430 | % | ISO 527-2 |
| Flexural Modulus - Chord 4(23°C) | 2240 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact - Flow | ASTM D256 | ||
| -30°C, 3.18 mm, Injection Molded | 80 | J/m | |
| 23°C, 3.18 mm, Injection Molded | No Break | ||
| Instrumented Dart Impact (0°C, Total Energy, Ductile Failure) | 35.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 100 | °C | ISO 75-2/Bf |
| CLTE - Flow (-30 to 100°C) | 4.3E-5 | cm/cm/°C | ASTM E831 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.18 mm, All Colors) | HB | UL 94 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60°, 3180 µm, Thermoformed, Smooth) | 20 to 40 | ISO 2813 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Sag - 8 inch span, two point support (149°C, 3.20 mm) | 0.00 | mm | ASTM D3769 |
| Note Message | |
|---|---|
| 1 . | Method A |
| 2 . | Type 1, 50 mm/min |
| 3 . | Type 1, 50 mm/min |
| 4 . | Type 1A, 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8983-80 White 1196 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| THERMOLAST® K TC5LEZ (Series: UV/FG) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Unilex™ UP 8002 | United Polychem | PP Homopolymer | Unilex™ |
| Cheng Yu FRV | Cheng Yu Plastic Company Limited | ABS | Cheng Yu |
| TECHNYL STAR® S 218L1 V30 BLACK 1N | Solvay Engineering Plastics | Nylon 6 | TECHNYL STAR® |