COSMOTHENE® EVA KA-31
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | TPC, The Polyolefin Company (Singapore) Pte Ltd |
| Trademark: | COSMOTHENE® EVA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | U9Em1p_COSMOTHENE-EVA-KA-31.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
COSMOTHENE EVA KA-31 is produced by the latest autoclave process technology licensed by Sumitomo Chemical Co. Japan. COSMOTHENE EVA KA-31 is a high strength EVA grade with good adhesioin strength and provides soft feeling for sheet application. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.945 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 7.0 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 28.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 26 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 11.8 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 800 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -50.0 | °C | JIS K7216 |
| Vicat Softening Temperature | 40.0 | °C | ASTM D1525 |
| Melting Temperature | 70.0 | °C | Internal Method |
| Ring and Ball Softening Point | > 150 | ASTM E28 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NYLOY® NG-0013N | Nytex Composites Co., Ltd. | Nylon 6 | NYLOY® |
| Aaroprene® ATPR 2040 | Aaron Industries Corp. | SEBS | Aaroprene® |
| BJB Polyurethane TC-890 A/B | BJB Enterprises, Inc. | PUR, Unspecified | BJB Polyurethane |
| EVALENE® PP PHF0702 | JG Summit Petrochemical Corporation | PP Homopolymer | EVALENE® PP |
| LEXAN™ 940 resin | SABIC Innovative Plastics | PC | LEXAN™ |