Vipel® F282-AAN-00

Category:	Polyester Alloy , Polyester Alloy
Manufacturer:	AOC, L.L.C.
Trademark:	Vipel®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	U974dH_Vipel-F282-AAN-00.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Vipel® Corrosion Resistant Bisphenol A, Fumarate Based Polyester Resin AOC's Vipel® F282 series resins are high molecular weight bisphenol A fumarate unsaturated polyester resins. Vipel® F282 series has an excellent shelf life and is ideal for filament winding and spray-up applications. One unique version is Vipel F282-ZZZ-00 which is the powdered alkyd product is an unique version that can be shipped abroad and blended locally with styrene or other monomers. Corrosion resistance Vipel® F282 is designed to make parts for a broad range of chemical environments such as acidic, bleach, hydrogen peroxide, oxidizing media, and caustic. Refer to AOC's "Corrosion Resistant Resin Guide" for corrosion resistance information or for questions regarding suitability of a resin to any particular chemical environment contact AOC. Versatile Suitable for various fabricating methods such as hand lay-up, spray-up, filament winding, etc. It is the fabricator's responsibility to also be sure that the final composite is well cured. All composites used for FDA applications should be post cured at 180°F/82°C for at least 4 hours. After post curing , laminate should be washed with soap and water and then rinsed.

Message

Vipel® Corrosion Resistant Bisphenol A, Fumarate Based Polyester Resin

AOC's Vipel® F282 series resins are high molecular weight bisphenol A fumarate unsaturated polyester resins. Vipel® F282 series has an excellent shelf life and is ideal for filament winding and spray-up applications. One unique version is Vipel F282-ZZZ-00 which is the powdered alkyd product is an unique version that can be shipped abroad and blended locally with styrene or other monomers.

Corrosion resistance
Vipel® F282 is designed to make parts for a broad range of chemical environments such as acidic, bleach, hydrogen peroxide, oxidizing media, and caustic. Refer to AOC's "Corrosion Resistant Resin Guide" for corrosion resistance information or for questions regarding suitability of a resin to any particular chemical environment contact AOC.

Versatile
Suitable for various fabricating methods such as hand lay-up, spray-up, filament winding, etc.

It is the fabricator's responsibility to also be sure that the final composite is well cured. All composites used for FDA applications should be post cured at 180°F/82°C for at least 4 hours. After post curing , laminate should be washed with soap and water and then rinsed.

General Information
Features	Acid Resistant Food Contact Acceptable Good Chemical Resistance Good Corrosion Resistance High Molecular Weight Oxidation Resistant
Uses	Coating Applications Filaments
Agency Ratings	FDA Unspecified Rating
Forms	Liquid
Processing Method	Filament Winding Hand Lay-up Spraying

Physical	Nominal Value	Unit
Specific Gravity	1.08	g/cm³
Styrene Content	50	%

Thermoset	Nominal Value	Unit
Exotherm
Gel to Peak	4.0	min
Peak	216	°C
Gel Time (82°C) ¹	12.0	min

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	3030	MPa	ASTM D638
Tensile Strength	70.3	MPa	ASTM D638
Tensile Elongation (Break)	2.6	%	ASTM D638
Flexural Modulus	3030	MPa	ASTM D790
Flexural Strength	119	MPa	ASTM D790

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed)	124	°C	ASTM D648

Thermoset	Nominal Value	Unit
Thermoset Mix Viscosity ²(25°C)	500	cP
Post Cure Time (82°C)	4.0	hr

Note Message
1 .	SPI gel with 1.0% BPO
2 .	LVSSA spindle 31 at 30 rpm

Resin Grade	Manufacturer	Category	Trademark
Sinpolene MBB0091	Teknor Apex Asia Pacific PTE. LTD.	LLDPE	Sinpolene
BCC Resins BC 100 Thick	BCC Products Inc.	EA	BCC Resins
EnviroNylon N6633HSL	West Michigan Compounding	Nylon 66	EnviroNylon
KRATON® G1652 H	Kraton Polymers LLC	SEBS	KRATON®
Hostacom EKC 265N 2 G82732	LyondellBasell Industries	PP Copolymer	Hostacom