Biograde® C 5508
| Category: | Biodeg Polymers , Biodegradable Polymers |
| Manufacturer: | FKuR Kunststoff GmbH |
| Trademark: | Biograde® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | U8oOmP_BiogradeC5508.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Biodegradable compound for injection moulding made partially from biobased recources |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.27 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/5.0 kg) | 18 - 25 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/5.0 kg) | 16.0 - 22.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 0.85 | % | ISO 294-4 |
| Flow | 0.39 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2460 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 55.0 | MPa | ISO 527-2 |
| Fracture | 53.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 17 | % | ISO 527-2 |
| Flexural Modulus | 2620 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 62.0 | MPa | ISO 178 |
| Tensile Strain at Tensile Strength | 7.0 | % | ISO 527 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 1 | 11 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 2 | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 107 | °C | ISO 306/A |
| Melting Temperature (DSC) | > 180 | °C | ISO 3146 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 190 | °C | |
| Middle Temperature | 190 | °C | |
| Front Temperature | 200 | °C | |
| Nozzle Temperature | 200 - 220 | °C | |
| Mold Temperature | 30 - 65 | °C |
| Injection instructions |
|---|
| Feeding zone: 60 °CHolding pressure level: 40 - 80 %Melt cushion (of volume): <10 %Cooling time: 10 sec.Max. dwell time: 300 sec. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 175 | °C | |
| Cylinder Zone 2 Temp. | 180 | °C | |
| Cylinder Zone 3 Temp. | 180 | °C | |
| Cylinder Zone 4 Temp. | 185 | °C |
| Extrusion instructions |
|---|
| Feeding zone: 60 °CWide slot nozzle 190 - 200 °CCalender roll temperature: 20 65 °C |
| Note Message | |
|---|---|
| 1 . | RT |
| 2 . | RT |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRE-ELEC® ESD 7100 | Premix Oy | ABS | PRE-ELEC® |
| Nylene® 5213-02 | Custom Resins Group | Nylon 6 | Nylene® |
| ASTALON™ GS2010R | Marplex Australia Pty. Ltd. | PC | ASTALON™ |
| Gallonprene® GP210-4004 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Hostacom PPU X9067HS G62490 | LyondellBasell Industries | PP Copolymer | Hostacom |