ULTEM™ PW2300 resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | U8YdrF_ULTEM-PW2300-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ULTEM PW2300 resin is an amorphous, opaque, 30% glass fiber reinforced polyetherimide (PEI) plastic offering a glass transition temperature (Tg) of 217°C. This inherently flame retardant resin is KTW, WRAS, ACS, NSF-61 and W270 certified and is US FDA and European Food Contact approved. ULTEM PW2300 resin offers specific colors designed and certified for use in potable water applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.51 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (360°C/5.0 kg) | 6.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 0.20 to 0.40 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.90 | % | |
| Equilibrium, 23°C, 50% RH | 0.50 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 165 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 165 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 8500 | MPa | ISO 178 |
| Flexural Stress | 225 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 20.0 | mg | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength 3 | ISO 179/1eU | ||
| -30°C | 40 | kJ/m² | |
| 23°C | 40 | kJ/m² | |
| Unnotched Izod Impact Strength 4 | ISO 180/1U | ||
| -30°C | 40 | kJ/m² | |
| 23°C | 40 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, Unannealed, 100 mm Span | 215 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 100 mm Span | 210 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 225 | °C | ISO 306/A50 |
| -- | 213 | °C | ISO 306/B50 |
| -- | 220 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 150°C | 2.0E-5 | cm/cm/°C | |
| Transverse : 23 to 150°C | 6.0E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.29 | W/m/K | ISO 8302 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 48 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 80.0 to 120 | °C | |
| Rear Temperature | 350 to 400 | °C | |
| Middle Temperature | 360 to 410 | °C | |
| Front Temperature | 370 to 420 | °C | |
| Nozzle Temperature | 360 to 410 | °C | |
| Processing (Melt) Temp | 370 to 410 | °C | |
| Mold Temperature | 140 to 180 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*4 |
| 5 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 301 FR HS UV | RTP Company | PC | RTP |
| VITAMIDE® AO3XBK6569 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| Xuchuan XCA-4035L | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Jampilen EP300L | Jam Polypropylene Company | PP Copolymer | Jampilen |
| Sylvin 8600-55 Blue 8360 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |