ACCUTECH™ HP0339T40L1
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | ACLO Compounders Inc. |
| Trademark: | ACCUTECH™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | U7tWyA_ACCUTECH-HP0339T40L1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ACCUTECH™HP0339T40L1 is a polypropylene homopolymer (PP Homopoly) product, which contains 40% talc filler. It is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 21 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.80 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 78 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 32.0 | MPa | ASTM D638 |
| Fracture | 30.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 3.0 | % | ASTM D638 |
| Fracture | 6.0 | % | ASTM D638 |
| Flexural Modulus | 4200 | MPa | ASTM D790 |
| Flexural Strength | 47.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 25 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 135 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 84.0 | °C | ASTM D648 |
| Additional Information |
|---|
| Ash Content, ASTM D2584: 40% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® PET IV 84 CB | Marco Polo International, Inc. | PET | MARPOL® PET |
| PTS PBT-101G0 | Polymer Technology and Services, LLC | PBT | PTS |
| VITAMIDE® AY36NT6104 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| ALTECH® PP-H FC 1000/100 DS | ALBIS PLASTIC GmbH | PP Homopolymer | ALTECH® PP-H |
| LNP™ LUBRICOMP™ DL001 compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |