ALCUDIA® EBA PA-1704
| Category: | EBA , Ethylene Butyl Acrylate Copolymer |
| Manufacturer: | REPSOL |
| Trademark: | ALCUDIA® EBA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | U7Rssa_ALCUDIA-EBA-PA-1704.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EBA copolymer ALCUDIA® PA-1704 is a copolymer suitable for blown film applications where good processability, flexibility and good mechanical properties are required. The butyl acrylate content is 17%. It contains antioxidant additives. EBA ALCUDIA® PA-1704 fulfils the food contact regulations in most countries. For further information or certificates, contact our Customer Service Offices. APPLICATIONS
Recommended melt temperature range is 160 to 180°C. EBA copolymers exhibit excellent thermal stability, which allows higher processing temperatures if needed. Processing characteristics of PA-1704 are similar to LDPE and conventional Polyethylene extruders are recommended. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.925 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.40 | g/10 min | ISO 1133 |
| n-Butyl Acrylate Content | 17.0 | wt% |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 100 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Broken, 100 µm, blown film | 20.0 | MPa | ISO 527-3 |
| TD : Broken, 100 µm, blown film | 22.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 100 µm, blown film | 700 | % | ISO 527-3 |
| TD : Broken, 100 µm, blown film | 800 | % | ISO 527-3 |
| Dart Drop Impact (100 µm, Blown Film) | > 1400 | g | ISO 7765-1 |
| Elmendorf Tear Strength 1 | ISO 6383-2 | ||
| MD : 100.0 µm | 36.0 | kN/m | ISO 6383-2 |
| TD : 100.0 µm | 39.0 | kN/m | ISO 6383-2 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Melting Temperature | 96.0 | °C |
| Additional Information |
|---|
| Data taken from 100 µm thickness film, blow up ratio 1:2.5, frost line height 50 cm. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 - 180 | °C |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Propafilm™ RGP140 | Innovia Films Ltd. | PP Alloy | Propafilm™ |
| TPUCO® TPUE-E95 | Taiwan PU Corporation | TPU-Polyester | TPUCO® |
| Gallonprene® GP210-7004 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Petroquim PP PH 2621 | Petroquim S.A. | PP Homopolymer | Petroquim PP |
| ESTOPLAST SR 1500IY01 | Ester Industries Ltd. | ABS | ESTOPLAST SR |