Petrotene® PP A2 G20 T10 PRTA011 PH204 MSP
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Petrotene® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | U6Rhbl_Petrotene-PP-A2-G20-T10-PRTA011-PH204-MSP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene with 20% fiberglass and 10% mineral filler, ideal for injection molding, resistant to oil, grease and many solvents, good set of mechanical properties and good dimensional stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 to 1.15 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 to 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.90 to 1.1 | % | ASTM D955 |
| Water Absorption (Equilibrium) | 0.050 | % | ASTM D570 |
| Ash Content | 28 to 32 | % | ASTM D2584 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Operating Temperature | 90 | °C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 30.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 50°C) | 15 | % | ASTM D638 |
| Flexural Modulus | 2500 | MPa | ASTM D790 |
| Flexural Strength | 45.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 30 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 65.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 150 | °C | ASTM D1525 2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 40 | kV/mm | ASTM D149 |
| Dissipation Factor (1 kHz) | 2.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 190 to 230 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Rate A (50°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SAXAMID™ 226K6 | SAX Polymers | Nylon 66 | SAXAMID™ |
| ALTECH® PA6 A 3230/500 GB15 GF15 | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| APEX® 3701-80NT1 | Teknor Apex Company | PVC, Flexible | APEX® |
| Gallonprene® GP520-5501 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| TOTAL Polyethylene TPSeal® M 3671 | TOTAL Refining & Chemicals | mPE | TOTAL Polyethylene |