| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | A. Schulman Inc. |
| Trademark: | ASI POLYPROPYLENE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | U6LftX_ASI-POLYPROPYLENE-3052X-01.pdf |
| PRICE: | Order Products email sales@su-jiao.com |
| Message |
|---|
| Polypropylene PP 3052X-01 is an extra high flow impact resistant copolymer with a relatively high stiffness. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 30 to 35 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 27.6 | MPa | ASTM D638 |
| Flexural Modulus | 1240 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 75 | J/m | ASTM D256 |
| Gardner Impact (-29°C) | 20.0 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 106 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 249 | RTP Company | Nylon 66 | RTP |
| Radiflam® A RV250 AF 875 BRU 3674 | Radici Plastics | Nylon 66 | Radiflam® |
| HiFill® PA6/6 GF43 LE BK | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| Kotex K-40UVR | Kotec Corporation | PC | Kotex |
| IROGRAN® A 85 P 4854 | Huntsman Corporation | TPU-Polyether | IROGRAN® |