Zytel® 80G33L NC010
| Category: | Nylon 66 , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | U6FGYn_Zytel-80G33L-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 33% Glass Reinforced, Toughened, Polyamide 66 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.32 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.80 | -- | % | |
| Flow | 0.30 | -- | % | |
| Water Absorption (24 hr) | 0.83 | -- | % | ASTM D570 |
| Viscosity Number | 165 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 8700 | 5800 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 142 | 95.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 4.0 | 5.0 | % | ISO 527-2 |
| Flexural Modulus | 7400 | 5200 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | 13 | 13 | kJ/m² | |
| -30°C | 14 | 14 | kJ/m² | |
| 23°C | 20 | 22 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 80 | 75 | kJ/m² | |
| 23°C | 91 | 80 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -40°C | 15 | 10 | kJ/m² | |
| -30°C | 14 | 10 | kJ/m² | |
| 23°C | 21 | 20 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 80 | 75 | kJ/m² | |
| 23°C | 74 | 80 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 262 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 247 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 262 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 1.5E-5 | -- | cm/cm/°C | |
| Transverse | 1.2E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.750 mm | HB | -- | ||
| 1.50 mm | HB | -- | ||
| Oxygen Index | 23 | -- | % | ISO 4589-2 |
| Fill Analysis | Dry | Conditioned | Unit | |
|---|---|---|---|---|
| Melt Density | 1.12 | -- | g/cm³ | |
| Specific Heat Capacity of Melt | 2200 | -- | J/kg/°C | |
| Thermal Conductivity of Melt | 0.22 | -- | W/m/K |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| StarFlex P 7335-9000 | STAR Thermoplastic Alloys & Rubbers, Inc. | TPE | Starflex |
| Sumitomo Epoxy E 8701A | Sumitomo Bakelite North America, Inc. | Epoxy | Sumitomo Epoxy |
| CERTENE™ 9814 Black | Muehlstein | PP, Unspecified | CERTENE™ |
| Chiao Fu PP PP212GB40 NAT | Chiao Fu Enterprises Co., Ltd. | PP, Unspecified | Chiao Fu PP |
| Geon™ Vinyl Dry Blend E0101 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Dry Blend |