SLOVALEN® PC 88 FRD 1
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Plastcom |
| Trademark: | SLOVALEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | U6CTGc_SLOVALEN-PC-88-FRD-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Modified copolymer PP with the possibility of changing the ITT-index within the interval 5 - 20 g/10 min. Stabilized against the UV-radiation and atmospheric conditions by the UV stabilizer on the HALS basis. Retarded with the halogen flame retardant. Application - stadium seats with guaranteed life-cycle of the mechanical and surface properties, electrical industry - terminals, coil forms, covers of electrotools, guides. Fulfills 960°C glow wire and flammability in accordance with UL 94 V2. Concerning flammability, it complies with the building norm DIN 4102- B2. Delivered in the full RAL colour scale. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.930 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ISO 1133 |
| Molding Shrinkage | STM 64 0808 | ||
| Across Flow | 2.4 | % | |
| Flow | 2.4 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1200 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 28.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 20 | % | ISO 527-2 |
| Flexural Modulus | 1000 | MPa | ISO 178 |
| Flexural Stress | 35.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 4.0 | kJ/m² | |
| 23°C | 9.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -20°C | 110 | kJ/m² | |
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 75.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 110 | °C | ISO 306/B |
| Melting Temperature (DSC) | 150 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength | 24 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (Solution A) | 450 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-2 | UL 94 | |
| Glow Wire Ignition Temperature | 960 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 200 to 250 | °C | |
| Mold Temperature | 30.0 to 50.0 | °C | |
| Injection Pressure | 50.0 to 80.0 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Andur 95-AP/Curene® 185 | Anderson Development Company | PUR-Ether/TDI | Andur |
| Karina BLUE COLOR CONCENTRATE 06/846-FC-LMP (SDB) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PENTAMID A GV30 HYD schwarz | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |
| Hostacom M4 N01 LG82767 | LyondellBasell Industries | PP Homopolymer | Hostacom |
| NORYL™ WCV072 resin | SABIC Innovative Plastics | PPE+PS+PP | NORYL™ |