Menzolit® CarbonSMC 1100 Datasheet,Polyester, TS,Menzolit Ltd (UK)-SHANGHAI SUSHENG

Message
Menzolit® CarbonSMC 1100 is a developmental carbon fibre SMC for high strength applications. The reinforcement has been put to a level that combines mouldability with high strength and stiffness properties. The specific resin and a high amount of carbon fibers provide high mechanical strength. Durability is improved as well. Even without a specific fire retardant, the fire retardancy level HB according UL 94 is achieved. Typical applictions are structural components within the automotive industry or mechanical engineering. It is suitable for load carrying applications or fast moving and accelerated components.

General Information
Filler / Reinforcement	Mineral filler Carbon fiber reinforced material, 30% filler by weight
Features	Low smoke Rigidity, high High strength Good formability Durability Halogen-free
Uses	Components Application in Automobile Field
Forms	Particle
Processing Method	Compression molding
Part Marking Code (ISO 11469)	>UP- CF60

Physical	Nominal Value	Unit	Test Method
Density	1.42	g/cm³	ISO 1183
Molding Shrinkage	-0.17	%	ISO 294-4
Water Absorption (Saturation, 23°C)	0.50	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (Compression Molded)	32000	MPa	ISO 527-2
Tensile Stress (Yield, Compression Molded)	138	MPa	ISO 527-2
Tensile Strain (Break, Compression Molded)	1.5	%	ISO 527-2
Flexural Modulus (Compression Molded)	28000	MPa	ISO 178
Flexural Stress (Compression Molded)	324	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (Compression Molded)	57	kJ/m²	ISO 179

Thermal	Nominal Value	Unit	Test Method
Glass Transition Temperature	162	°C	DSC
CLTE - Flow	8.0E-6	cm/cm/°C	ISO 11359-2

Flammability	Nominal Value		Test Method
Flame Rating (2.00 mm)	HB		UL 94

Additional Information
Fibre Content UD, total EN ISO 1172: 60%Post Moulding Shrinkage DIN 53464: 0,00%Heat Distortion Temp. EN ISO 75-2: >200°CGlass Transition Temp. ISO 11357-2: 162°CContinous Service Temp. Menzolit method: 170°CPoison's Ratio Menzolit method: 0,30Matrix Crazing Strain Menzolit method: 0,50%Compression Strength EN ISO 14126: 140 MPaThe value listed as Molding Shrinkage ISO 294-4, was tested in accordance with ISO 2577.The values listed as Flexural Strength and Flexural Modulus, ISO 178, were tested in accordance with EN ISO 14125.

Additional Information

Fibre Content UD, total EN ISO 1172: 60%Post Moulding Shrinkage DIN 53464: 0,00%Heat Distortion Temp. EN ISO 75-2: >200°CGlass Transition Temp. ISO 11357-2: 162°CContinous Service Temp. Menzolit method: 170°CPoison's Ratio Menzolit method: 0,30Matrix Crazing Strain Menzolit method: 0,50%Compression Strength EN ISO 14126: 140 MPaThe value listed as Molding Shrinkage ISO 294-4, was tested in accordance with ISO 2577.The values listed as Flexural Strength and Flexural Modulus, ISO 178, were tested in accordance with EN ISO 14125.

Injection	Nominal Value	Unit
Mold Temperature	155 - 160	°C
Injection Pressure	5.00 - 12.0	MPa

Category:	Polyester, TS , Thermoset Polyester
Manufacturer:	Menzolit Ltd (UK)
Trademark:	Menzolit®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	U61uWK_Menzolit-CarbonSMC-1100.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Chemraz 656	Greene, Tweed & Co.	Perfluoroelastomer	Chemraz
Ferro PP TPP20AJ34NA	Ferro Corporation	PP Homopolymer	Ferro PP
Jamplast Ex-04 ABS	Jamplast, Inc.	ABS	Jamplast
OnColor™ CC10075093WE	PolyOne Corporation	TP, Unspecified	OnColor™
Paryls® PSU F3150GL30	Youju New Materials Co., Ltd.	PSU	Paryls®