EGYPTENE LL 0220 KJ
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Sidpec (Sidi Kerir Petrochemicals Co.) |
| Trademark: | EGYPTENE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | U5TRFv_EGYPTENE-LL-0220-KJ.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LL 0220 KJ is a LLDPE copolymer with butane as comonomer which contains antioxidant, slip and antiblock additives. This grade is suitable for the production of blown film for light duty applications with a high slip requirement. Film made from pure LL 0220 KJ can be produced at higher output compared to standard 1MFR LDPE buttene copolymers. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ISO 1872-1 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 1184 | ||
| MD : Yield | 10.0 | MPa | ISO 1184 |
| TD : Yield | 11.0 | MPa | ISO 1184 |
| MD : Fracture | 30.0 | MPa | ISO 1184 |
| TD : Fracture | 25.0 | MPa | ISO 1184 |
| Tensile Elongation | ISO 1184 | ||
| MD : Fracture | 650 | % | ISO 1184 |
| TD : Fracture | 800 | % | ISO 1184 |
| Dart Drop Impact | 100 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm | 100 | g | ASTM D1922 |
| TD : 25 µm | 270 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 93.0 | °C | ISO 306 |
| Additional Information |
|---|
| Film properties were measured on 38 micron film extruded at a blow up ratio 2:1 with a melt temperature of 225°C. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reny® C-408 | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| Trademark PE mLLD1918C | Trademark Plastics Corporation | mLLDPE | Trademark PE |
| Tufel® II 94406 | Momentive Performance Materials Inc. | Silicone | Tufel® II |
| AKROMID® B3 ICF 10 1 L black (5514) | AKRO-PLASTIC GmbH | Nylon 6+PP | AKROMID® |
| LEXAN™ EXL1434 resin | SABIC Innovative Plastics | PC | LEXAN™ |