Arnitel® CM551
| Category: | Copolyester , Copolyester |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Arnitel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | U4Aebn_Arnitel-CM551.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Arnitel® CM551 is a Copolyester material. It is available in Asia Pacific, Europe, or North America. Primary attribute of Arnitel® CM551: Heat Resistant. |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 8.00 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 3 sec) | 51 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 140 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 32.0 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break | 450 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | No Break | ISO 179/1eA | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -20°C | 9.0 | kJ/m² | |
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 170 | °C | ISO 306/B50 |
| Melting Temperature 1 | 205 | °C | ISO 11357-3 |
| CLTE - Transverse | 1.9E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 15 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 4.34 | ||
| 1 MHz | 3.58 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 0.021 | ||
| 1 MHz | 0.046 | ||
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 200 to 220 | °C | |
| Middle Temperature | 210 to 230 | °C | |
| Front Temperature | 220 to 240 | °C | |
| Nozzle Temperature | 230 to 250 | °C | |
| Processing (Melt) Temp | 230 to 250 | °C | |
| Mold Temperature | 20.0 to 50.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Fluoroplex F 30 - GML | UNIFLON | PTFE | Fluoroplex |
| Hylon® N5116MGHL | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| ESTOPLAST ZK 6230NN02 | Ester Industries Ltd. | PC | ESTOPLAST ZK |
| TOTAL Polystyrene Impact 4440H | TOTAL Refining & Chemicals | PS (HIPS) | TOTAL Polystyrene |
| Moplen HP400K | LyondellBasell Industries | PP Homopolymer | Moplen |