Premi-Glas® 1200H-20
| Category: | TS, Unspecified , Thermoset, Unspecified |
| Manufacturer: | Premix, Inc. |
| Trademark: | Premi-Glas® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | U2mbmc_Premi-Glas-1200H-20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Premi-Glas® 1200H-20 is a fiberglass-reinforced thermoset sheet molding compound for general purpose applications requiring thermal stability and stiffness. Key Features and Benefits:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage | 0.010 | % | ISO 294-4 |
| Outdoor Suitability | f1 | UL 746C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Compression Molded) | 11700 | MPa | ASTM D638 |
| Tensile Strength (Compression Molded) | 48.3 | MPa | ASTM D638 |
| Flexural Modulus (Compression Molded) | 10300 | MPa | ASTM D790 |
| Flexural Strength (Compression Molded) | 124 | MPa | ASTM D790 |
| Compressive Strength 1 | 165 | MPa | ASTM D695 |
| Poisson's Ratio | 0.30 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 530 | J/m | ASTM D256 |
| Unnotched Izod Impact (Compression Molded) | 800 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE | |||
| Flow 2 | 2.5E-5 | cm/cm/°C | |
| Transverse 3 | 3.5E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.30 | W/m/K | |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 130 | °C | UL 746 |
| RTI Str | 130 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength 4 | 15 | kV/mm | ASTM D149 |
| Arc Resistance 5 | 180 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.52 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | Compression Molded |
| 2 . | XY Direction |
| 3 . | Z Direction |
| 4 . | Compression Molded |
| 5 . | Compression Molded |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYMAN® (ABS) K1836 | A. Schulman Europe | ABS | POLYMAN® |
| RTP PA66 20 GF FR0 BLK | RTP Company | Nylon 66 | RTP |
| Edgetek™ ET9200-5006 FD NATURAL | PolyOne Corporation | PPS | Edgetek™ |
| INEOS PP 240xGB08 | INEOS Olefins & Polymers Europe | PP Random Copolymer | INEOS PP |
| POLYabs F00 GF15 | Polykemi AB | ABS | POLYabs |