TAROMID B 280 MT5 Y2
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROMID B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | U1Vq4F_TAROMID-B-280-MT5-Y2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6, 25% mineral filled, UL94 V2 halogen free flame retarded, good flame proofing also at low thickness, good flow and good mechanical properties. High CTI value. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.60 | % | |
| Across Flow | 0.60 | % | |
| Water Absorption | |||
| 23°C, 24 hr | 1.5 | % | ASTM D570, ISO 62 |
| Saturation | 6.0 | % | ASTM D570 |
| Saturation, 23°C | 6.0 | % | ISO 62 |
| Granule Humidity | < 0.10 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4100 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Break) | 75.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 3.5 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 4400 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 115 | MPa | ISO 178 |
| Break | 115 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 1(23°C) | 3.0 | kJ/m² | ASTM D256, ISO 179 |
| Charpy Unnotched Impact Strength 2(23°C) | 50 | kJ/m² | ASTM D256, ISO 179 |
| Notched Izod Impact | |||
| 23°C, 3.20 mm | 50 | J/m | ISO 180, ASTM D256 |
| -- | 3.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 170 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | 200 | °C | ISO 306/B50, ASTM D1525 3 |
| Melting Temperature | 222 | °C | ASTM D211, ISO 121 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.970 mm) | V-2 | UL 94 | |
| Glow Wire Ignition Temperature (1.00 mm) | 960 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 to 90.0 | °C | |
| Pre-heater | 80.0 to 100 | °C | |
| Drying Time | |||
| -- | 1.0 | hr | |
| Pre-heater | 3.0 | hr | |
| Processing (Melt) Temp | 250 to 280 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 6x4x50 mm |
| 2 . | 6x4x50 mm |
| 3 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| YUPLENE® B34A | SK Global Chemical | PP Impact Copolymer | YUPLENE® |
| Nypol® PA A3 G15 P7 M1 S1 NTLA014 NR335 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Duratel MF3 | Custom Resins Group | Acetal (POM) Copolymer | Duratel |
| Plexar® PX3610 | LyondellBasell Industries | LLDPE | Plexar® |
| NORYL™ N1150 resin | SABIC Innovative Plastics Asia Pacific | PPE+PS | NORYL™ |