Plexiglas® Optical POQ62

Category:	Acrylic (PMMA) , Polymethyl Methacrylate Acrylic
Manufacturer:	Evonik Industries AG
Trademark:	Plexiglas®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	TzvyPT_Plexiglas-Optical-POQ62.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Product Profile:
PLEXIGLAS® Optical POQ62 is an amorphous thermoplastic molding compound based on polymethylmethacrylate (PMMA).

In addition to the familiar properties of PLEXIGLAS® molding compounds, such as

excellent light transmission and brilliance,

very good weather resistance,

high mechanical strength, surface hardness and mar resistance,

PLEXIGLAS® Optical POQ62 is distinguished by its

guaranteed purity and clarity,

outstanding flow properties due to its low melt viscosity and its

extremely accurate mold surface reproduction.

Application:
PLEXIGLAS® Optical POQ62 is particularly suitable for injection-compression molding and for injection-molding thin-walled parts with long flow paths. Further fields of application are two-component injection molding and special extrusion.

Examples:
Manufacture of moldings with microstructured surfaces and optical structures.

General Information
Features	Good Flow Good Weather Resistance High Clarity High Hardness High Strength Light Stabilized
Uses	Optical Applications
Forms	Pellets
Processing Method	Extrusion Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	1.19	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (230°C/3.8 kg)	21.0	cm³/10min	ISO 1133
Water Absorption (Equilibrium, 23°C, 50% RH)	0.60	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	3300	MPa	ISO 527-2/1
Tensile Stress (Break)	63.0	MPa	ISO 527-2/5
Tensile Strain (Break)	2.8	%	ISO 527-2/5

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength (23°C)	20	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	97.0	°C	ISO 306/B50
CLTE - Flow (0 to 50°C)	8.0E-5	cm/cm/°C	ISO 11359-2

Flammability	Nominal Value		Test Method
Fire Rating	B2		DIN 4102

Optical	Nominal Value	Unit	Test Method
Refractive Index	1.490		ISO 489
Transmittance ¹	92.0	%	ISO 13468-2
Haze	< 0.50	%	ASTM D1003

Injection	Nominal Value	Unit
Drying Temperature	< 80.0	°C
Drying Time	2.0 to 3.0	hr
Processing (Melt) Temp	220 to 260	°C
Mold Temperature	60.0 to 90.0	°C

Note Message
1 .	D65

Resin Grade	Manufacturer	Category	Trademark
MIDILENA III PPF401NTT	ROMPETROL PETROCHEMICALS S.R.L.	PP Homopolymer	MIDILENA III
Lucky Enpla LPC1000R	Lucky Enpla Co LTD	PC	Lucky Enpla
Plenco 07080 (Compression)	Plastics Engineering Co.	Phenolic	Plenco
Sylvin 6034-85 Blue 8426	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
REV Materials 8011	REV Materials	Polyolefin, Unspecified	REV Materials