VALOX™ DR48 resin
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TzgmQW_VALOXDR48resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| VALOX DR48 is a 17% glass reinforced, flame retardant injection moulding PBT resin. Applications: lamp sockets, connectors, switches, electrical housings and bases, bobbins, trimmers and electromotor housings. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.51 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (266°C/5.0 kg) | 90 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 250°C/2.16 kg | 14.0 | cm³/10min | ISO 1133 |
| 250°C/5.0 kg | 40.0 | cm³/10min | ISO 1133 |
| 265°C/5.0 kg | 70.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage 1 | Internal method | ||
| Flow | 0.50 - 0.80 | % | Internal method |
| Transverse flow | 0.60 - 0.90 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.17 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.070 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ISO 2039-2 | |
| Ball Indentation Hardness (H 358/30) | 218 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 7100 | MPa | ASTM D638 |
| -- | 7000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 3 | 100 | MPa | ASTM D638 |
| Yield | 104 | MPa | ISO 527-2/5 |
| Fracture 4 | 100 | MPa | ASTM D638 |
| Fracture | 104 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 5 | 2.0 | % | ASTM D638 |
| Yield | 2.0 | % | ISO 527-2/5 |
| Fracture 6 | 2.0 | % | ASTM D638 |
| Fracture | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 7 | 5400 | MPa | ASTM D790 |
| -- 8 | 6100 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 155 | MPa | ISO 178 |
| Yield, 50.0mm span 9 | 130 | MPa | ASTM D790 |
| Fracture, 50.0mm span 10 | 130 | MPa | ASTM D790 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 16.0 | mg | Internal method |
| Flexural Strain at Break 11 | 3.0 | % | ISO 178 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Filler Content | 17 | % | ASTM D229 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30°C 12 | 4.0 | kJ/m² | ISO 179/1eA |
| -30°C | 5.0 | kJ/m² | ISO 179/2C |
| 23°C 13 | 5.0 | kJ/m² | ISO 179/1eA, ISO 179/2C |
| Charpy Unnotched Impact Strength | |||
| -30°C 14 | 20 | kJ/m² | ISO 179/1eU |
| -30°C | 24 | kJ/m² | ISO 179/2U |
| 23°C 15 | 25 | kJ/m² | ISO 179/1eU |
| 23°C | 24 | kJ/m² | ISO 179/2U |
| Notched Izod Impact | |||
| -30°C | 45 | J/m | ASTM D256 |
| 0°C | 45 | J/m | ASTM D256 |
| 23°C | 45 | J/m | ASTM D256 |
| -30°C 16 | 5.0 | kJ/m² | ISO 180/1A |
| 0°C 17 | 5.0 | kJ/m² | ISO 180/1A |
| 23°C 18 | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| -30°C | 280 | J/m | ASTM D4812 |
| 23°C | 280 | J/m | ASTM D4812 |
| -30°C 19 | 20 | kJ/m² | ISO 180/1U |
| 23°C 20 | 20 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 215 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 100 mm span 21 | 215 | °C | ISO 75-2/Be |
| 0.45 MPa, unannealed, 64.0mm span 22 | 210 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 190 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 100 mm span 23 | 185 | °C | ISO 75-2/Ae |
| 1.8 MPa, unannealed, 64.0mm span 24 | 180 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 199 | °C | ASTM D1525, ISO 306/B120 14 25 |
| -- | 218 | °C | ASTM D1525, ISO 306/A50 15 26 |
| -- | 198 | °C | ISO 306/B50 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : -40 to 40°C | 2.8E-5 | cm/cm/°C | ISO 11359-2 |
| Flow : 23 to 80°C | 3.5E-5 | cm/cm/°C | ISO 11359-2 |
| Flow : 23 to 150°C | 2.6E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 80°C | 9.5E-5 | cm/cm/°C | ISO 11359-2 |
| Horizontal : 23 to 150°C | 1.5E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.19 | W/m/K | ISO 8302 |
| RTI Elec | 120 | °C | UL 746 |
| RTI Imp | 120 | °C | UL 746 |
| RTI | 140 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | |||
| 0.800 mm, in Oil | 29 | kV/mm | ASTM D149 |
| 1.60 mm, in Oil | 23 | kV/mm | ASTM D149 |
| 3.20 mm, in Oil | 16 | kV/mm | ASTM D149 |
| 0.800mm, in oil | 29 | kV/mm | IEC 60243-1 |
| 1.00 mm 27 | 19 | kV/mm | IEC 60243-1 |
| 1.60mm, in oil | 23 | kV/mm | IEC 60243-1 |
| 3.20mm, in oil | 16 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 1 MHz | 3.10 | ASTM D150, IEC 60250 | |
| 50 Hz | 3.20 | IEC 60250 | |
| 60 Hz | 3.20 | IEC 60250 | |
| Dissipation Factor | |||
| 1 MHz | 0.012 | ASTM D150, IEC 60250 | |
| 50 Hz | 1.0E-3 | IEC 60250 | |
| 60 Hz | 1.0E-3 | IEC 60250 | |
| Arc Resistance 28 | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 | |
| Comparative Tracking Index | IEC 60112 | ||
| -- | 175 | V | IEC 60112 |
| Solution B | 150 | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 4 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.890 mm | V-0 | UL 94 | |
| 3.00 mm | 5VA | UL 94 | |
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Oxygen Index | 31 | % | ISO 4589-2 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (260°C, 1500 sec^-1) | 105 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 120 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 40.0 - 60.0 | °C | |
| Rear Temperature | 230 - 245 | °C | |
| Middle Temperature | 240 - 255 | °C | |
| Front Temperature | 245 - 265 | °C | |
| Nozzle Temperature | 240 - 260 | °C | |
| Processing (Melt) Temp | 250 - 270 | °C | |
| Mold Temperature | 40.0 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | Type 1, 5.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 1.3 mm/min |
| 11 . | 2 mm/min |
| 12 . | 80*10*4 sp=62mm |
| 13 . | 80*10*4 sp=62mm |
| 14 . | 80*10*4 sp=62mm |
| 15 . | 80*10*4 sp=62mm |
| 16 . | 80*10*4 |
| 17 . | 80*10*4 |
| 18 . | 80*10*4 |
| 19 . | 80*10*4 |
| 20 . | 80*10*4 |
| 21 . | 120*10*4 mm |
| 22 . | 80*10*4 mm |
| 23 . | 120*10*4 mm |
| 24 . | 80*10*4 mm |
| 25 . | 标准 B (120°C/h), 载荷2 (50N) |
| 26 . | 速率 A (50°C/h), 载荷2 (50N) |
| 27 . | Short-Time |
| 28 . | Tungsten electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® S CT300 333 NER | Radici Plastics | Nylon 6 | Radilon® |
| Rhelon G1523-01 | RheTech, Inc. | Nylon 6 | Rhelon |
| Shin-Etsu RTV KE-1871 | Shin-Etsu Silicones of America | Silicone Rubber, RTV-1 | Shin-Etsu RTV |
| Starflam P10002Z | Eurostar Engineering Plastics | Nylon 6 | Starflam |
| Karina BEIGE PVC COMP. -E 856-08/151-Y-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |