RheTech Thermoplastic Polyolefin FT7012-707UV
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | RheTech, Inc. |
| Trademark: | RheTech Thermoplastic Polyolefin |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Tvoenn_RheTech-Thermoplastic-Polyolefin-FT7012-707UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Thermoplastic Polyolefin, 170K Flexural Modulus, UV Stabilized, 848 Black. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 60 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 16.5 | MPa | ASTM D638 |
| Flexural Modulus | 1170 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 800 | J/m | ASTM D256 |
| Dart Drop Impact | 20.3 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 80.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 45.0 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 - 82.2 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 204 - 232 | °C | |
| Middle Temperature | 210 - 238 | °C | |
| Front Temperature | 216 - 243 | °C | |
| Nozzle Temperature | 221 - 232 | °C | |
| Mold Temperature | 26.7 - 48.9 | °C | |
| Injection Pressure | 2.76 - 10.3 | MPa | |
| Holding Pressure | 2.07 - 8.27 | MPa | |
| Back Pressure | 0.345 - 1.03 | MPa |
| Injection instructions |
|---|
| Injection Speed: Variable - Application DependentScrew RPM: Recovery 3 seconds before mold opensCycle Time: Wall Thickness Dependent |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® PSC 6020 | Marco Polo International, Inc. | PS (GPPS) | MARPOL® PSC |
| Fainplast PVC GS 6612 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Elvamide® 8063 | DuPont Performance Polymers | Nylon, Unspecified | Elvamide® |
| LUVOCOM® 1-7893/GY VP | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| Complet® LCF15-LGF35-TPU | PlastiComp, Inc. | ETPU | Complet® |