EL-Pro™ P440J
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | SCG Chemicals Co., Ltd. |
| Trademark: | EL-Pro™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TugsCq_EL-Pro-P440J.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EL-Pro P440J is an impact copolymer polypropylene resin suitable for injection molding process. This resin is recommended for product that requires high impact strength with good processibility. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 2.00mm | 1.2 | % | ASTM D955 |
| Transverse flow : 2.00mm | 1.1 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 60 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength - Across Flow 1 | ASTM D638 | ||
| Yield | 26.5 | MPa | ASTM D638 |
| Fracture | 19.6 | MPa | ASTM D638 |
| Flexural Modulus | 1230 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 49 | J/m | ASTM D256 |
| 0°C | 59 | J/m | ASTM D256 |
| 23°C | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 100 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 55.0 | °C | ASTM D648 |
| Brittleness Temperature | -20.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 150 | °C | ASTM D1525 |
| Melting Temperature | 120 - 163 | °C | ASTM D2117 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 230 - 270 | °C | |
| Mold Temperature | 25.0 - 70.0 | °C | |
| Injection Rate | Fast | ||
| Screw Speed | 40 - 70 | rpm |
| Injection instructions |
|---|
| Injection Pressure: 40 to 80% of max. pressurePacking and Holding Pressure: 30 to 60% of max. pressureBack Pressure: 10% of max. pressure |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Verolloy DR210 | PlastxWorld Inc. | PC+SMA | Verolloy |
| CompaDur® 125 GF 15 black (042) | DimeLika Plast GmbH | PBT+PET | CompaDur® |
| Evoprene™ 3273 | AlphaGary | SBS | Evoprene™ |
| Karina CLEAR PVC COMPOUND 75/204-D-AT-IS-H (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ STAT-KON™ AE004 compound | SABIC Innovative Plastics | ABS | LNP™ STAT-KON™ |