NuSil MED4-4115

Category:	Rubber , Rubber
Manufacturer:	NuSil Technology
Trademark:	NuSil
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	TtfGoW_NuSil-MED4-4115.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
NuSil Technology's restricted materials may be considered for use in short-term implant applications, 29 days or less, or for external applications. HCRs can be used for extrusion of tubing and profiles (rod or ribbon), in calendared sheeting for die-cutting, or in compression or transfer molded parts such as balloons, gaskets or o-rings. HCRs are clay-like in the uncured state and when cured generally exhibit very high mechanical properties and low modulus. HCRs with a peroxide cure system have a long history in implant applications.The cure mechanism can be vinyl specific or non vinyl specific. Non vinyl specific peroxide catalysts are more commonly used with HCRs than vinyl specific peroxide catalysts. Comments: NON-VINYL SPECIFIC PEROXIDE PRECATALYZED

Message

NuSil Technology's restricted materials may be considered for use in short-term implant applications, 29 days or less, or for external applications.

HCRs can be used for extrusion of tubing and profiles (rod or ribbon), in calendared sheeting for die-cutting, or in compression or transfer molded parts such as balloons, gaskets or o-rings. HCRs are clay-like in the uncured state and when cured generally exhibit very high mechanical properties and low modulus.

HCRs with a peroxide cure system have a long history in implant applications.The cure mechanism can be vinyl specific or non vinyl specific. Non vinyl specific peroxide catalysts are more commonly used with HCRs than vinyl specific peroxide catalysts.

Comments: NON-VINYL SPECIFIC PEROXIDE PRECATALYZED

General Information
Uses	Washer Pipe fittings Balloon application Profile Medical/nursing supplies
Agency Ratings	USP Class VI
Processing Method	Extrusion Resin transfer molding Profile extrusion molding Compression molding Calendering

Mechanical	Nominal Value	Unit
Tensile Strength (200% Strain)	3.10	MPa

Thermoset	Nominal Value	Unit
Post Cure Time (249°C)	2.0	hr

Additional Information	Nominal Value	Unit
Cure System	Peroxide
Plasticity: 90 mils

Uncured Properties	Nominal Value	Unit
Density	1.15	g/cm³
Curing Time (116°C)	0.083	hr

Cured Properties	Nominal Value	Unit
Shore Hardness (Shore A)	50
Tensile Strength	10.3	MPa
Tensile Elongation at Break	450	%
Tear Strength	17.5	kN/m

Resin Grade	Manufacturer	Category	Trademark
Sylvin 8627-90 Black	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
Nypol® PA A3 G30 M2 NTLA014 NR394 MSP	Petropol Industry and Trade of Polymers LTDA	Nylon 66	Nypol® PA
BJB Polyurethane TC-421 A/B-C CASTABLE	BJB Enterprises, Inc.	TSU	BJB Polyurethane
Bergamid™ B700 G30 H GR255	PolyOne Corporation	Nylon 6	Bergamid™
LUVOCOM® 80-8842	Lehmann & Voss & Co.	Acetal (POM) Copolymer	LUVOCOM®