Plexiglas® VS-UVT
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Altuglas International of Arkema Inc. |
| Trademark: | Plexiglas® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TtegHV_Plexiglas-VS-UVT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Plexiglas® VS-UVT is a thermoplastic acrylic resin suitable for injection molding. It is a high flow resin designed to provide exceptional UV transmission and excellent transparency making it an outstanding choice for in-vitro diagnostic applications. Some of the features and benefits of Plexiglas® VS-UVT are:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 27 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.20 to 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 84 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2900 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 64.8 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 2960 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 96.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 16 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 1 | ASTM D648 | ||
| 0.45 MPa, Annealed | 80.6 | °C | |
| 1.8 MPa, Annealed | 76.1 | °C | |
| Vicat Softening Temperature | |||
| -- | 87.2 | °C | ASTM D1525 2 |
| -- | 81.1 | °C | ASTM D1525 3 |
| Thermal Conductivity | 0.19 | W/m/K | ASTM C177 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index 4 | 1.490 | ASTM D542 | |
| Transmittance (3180 µm) | 92.0 | % | ASTM D1003 |
| Haze (3180 µm) | < 1.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ASTM Classification | PMMA 0112V7 | ASTM D788 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 to 76.7 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Suggested Shot Size | 50 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 182 | °C | |
| Middle Temperature | 188 | °C | |
| Front Temperature | 193 | °C | |
| Nozzle Temperature | 188 | °C | |
| Processing (Melt) Temp | < 271 | °C | |
| Mold Temperature | 48.9 to 65.6 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.689 | MPa | |
| Screw Speed | 50 to 100 | rpm | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 | ||
| Screw Compression Ratio | 2.0:1.0 to 2.5:1.0 | ||
| Vent Depth | 0.051 | mm |
| Note Message | |
|---|---|
| 1 . | Annealing cycle: 4hrs @ 158°F |
| 2 . | Rate A (50°C/h), Loading 1 (10 N) |
| 3 . | Rate A (50°C/h), Loading 2 (50 N) |
| 4 . | ND @ 72°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VESTOLIT® P 1353 K | VESTOLIT GmbH & Co. KG | PVC Homopolymer | VESTOLIT® |
| Chemical Resources PET08512 | Chemical Resources, Inc. | PET | Chemical Resources |
| Epocast 1629 A/B | Huntsman Advanced Materials | Epoxy | Epocast |
| Karina COMP. PVC IVORY 813-35/ 1-DY-SN-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Polyrocks 1001T | Polyrocks Chemical Co., Ltd | PC | Polyrocks |