Multilon® T-2830R
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | TEIJIN LIMITED |
| Trademark: | Multilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Tpuu1Y_Multilon-T-2830R.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC/ABS polymer alloy |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 250°C/5.0 kg | 18.0 | cm³/10min | |
| 260°C/5.0 kg | 28.0 | cm³/10min | |
| Molding Shrinkage 1 | Internal Method | ||
| Across Flow : 4.00 mm | 0.50 to 0.70 | % | |
| Flow : 4.00 mm | 0.50 to 0.70 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2250 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 52.0 | MPa | |
| Break | 55.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 3.0 | % | |
| Break | 120 | % | |
| Flexural Modulus 2 | 2150 | MPa | ISO 178 |
| Flexural Stress 3 | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 35 | kJ/m² | |
| 23°C | 50 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 125 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 102 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 120 | °C | ISO 306/B50 |
| CLTE | ISO 11359-2 | ||
| Flow | 8.0E-5 | cm/cm/°C | |
| Transverse | 8.0E-5 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | Mold shrinkage of Multilon will vary depending on its application thickness. |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumikon® PM-6930H | Sumitomo Bakelite Co., Ltd. | Phenolic | Sumikon® |
| Sylvin 8250-65 Natural | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| MOSTEN FK 005 | UNIPETROL RPA | PP Homopolymer | MOSTEN |
| Hanwha Total PP BJ600 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP Impact Copolymer | Hanwha Total PP |
| Infino HC-8040 | LOTTE ADVANCED MATERIALS CO., LTD. | Nylon+PPE | Infino |