Spartech Polycom SCR2-1090

Category:	PS (HIPS) , High Impact Polystyrene
Manufacturer:	Spartech Polycom
Trademark:	Spartech
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	ToxyBV_Spartech-Polycom-SCR2-1090.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Spartech SCR2-1090 is a medium viscosity, high impact polystyrene (HIPS) resin for injection molding. It is heat stabilized and lubricated for good processing characteristics.

HIPS are rubber modified styrenics that typically contain 1-10% rubber by weight. They offer dimensional and physical stability in moist environments and provide good chemical resistance. These materials also exhibit good flexibility along with good toughness.

A very versatile product for a wide variety of applications, Spartech SCR2-1090 is recommended for industrial, transportation, sporting goods and electrical/electronic applications.

General Information
Additive	heat stabilizer Lubricant
Features	Good dimensional stability Impact resistance, good Workability, good Good flexibility Good chemical resistance Thermal Stability Thermal stability, good Good toughness Lubrication Medium viscosity
Uses	Electrical/Electronic Applications Industrial application Application in Automobile Field Sporting goods
Appearance	Available colors Natural color
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Melt Mass-Flow Rate (MFR)	9.0	g/10 min	ASTM D1238

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (23°C)	22.8	MPa	ASTM D638
Tensile Elongation (Break, 23°C)	40	%	ASTM D638
Flexural Modulus (23°C)	2410	MPa	ASTM D790
Flexural Strength (23°C)	43.4	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C)	130	J/m	ASTM D256

Injection	Nominal Value	Unit
Drying Temperature	71.1 - 82.2	°C
Drying Time	2.0	hr
Rear Temperature	200 - 220	°C
Middle Temperature	205 - 225	°C
Front Temperature	210 - 230	°C
Nozzle Temperature	210 - 230	°C
Processing (Melt) Temp	191 - 260	°C
Mold Temperature	26.7 - 48.9	°C

Resin Grade	Manufacturer	Category	Trademark
Shuman PPO 211	Shuman Plastics, Inc.	PPE+PS	Shuman PPO
Starex EA-0640	SAMSUNG SDI CO., LTD.	ABS	Starex
Arlon® 3000 XT	Greene, Tweed & Co.	PEEK	Arlon®
Cri-Line HFLT-720	Cri-Tech, Inc.	Fluorelastomer	Cri-Line
Fainplast PVC FK 0635	Fainplast Compounds S.r.l	PVC, Unspecified	Fainplast PVC