Alathon® XL5906WC
| Category: | HDPE, HMW , High Density (HMW) Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Alathon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TnwU4Z_Alathon-XL5906WC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ALATHON XL 5906WC is a high molecular weight high density homopolymer with a broad bimodal molecular weight distribution. This resin exhibits excellent stiffness and very high tensile strength. Typical applications for wire and cable include optical fiber buffer tubes. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.959 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.057 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (10% Igepal, Compression Molded, F50) | 96.0 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 69 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, molding | 29.6 | MPa | ASTM D638 |
| Fracture, molding | 40.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, Compression Molded) | 900 | % | ASTM D638 |
| Flexural Modulus - 1% Secant (Compression Molded) | 1470 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 130 | °C | ASTM D1525 |
| CLTE - Flow | 1.4E-4 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 7.6E+17 | ohms·cm | ASTM D257 |
| Dielectric Constant (1 MHz) | 2.36 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 5.0E-5 | ASTM D150 |
| Additional Information |
|---|
| The value listed as Dielectric Constant, ASTM D150, was tested in accordance with ASTM D1531.The value listed as Dissipation Factor, ASTM D150, was tested in accordance with ASTM D1531.Thermal Stress Crack Resistance, ASTM D2951, F50, compression molded: >264 hr |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 149 - 163 | °C | |
| Cylinder Zone 2 Temp. | 177 - 204 | °C | |
| Cylinder Zone 3 Temp. | 204 - 232 | °C | |
| Cylinder Zone 4 Temp. | 246 - 260 | °C | |
| Adapter Temperature | 246 - 260 | °C | |
| Melt Temperature | 246 - 260 | °C | |
| Die Temperature | 246 - 260 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| StarTwist™ 315XT (transparent) | Innovia Films Ltd. | CA | StarTwist™ |
| Sylvin 8325-70 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| VESTAMID® L L1670 | Evonik Industries AG | Nylon 12 | VESTAMID® L |
| HONES® PBT GF10 | Guangdong Shunde Hones Polymer Material Co., Ltd. | PBT | HONES® |
| LNP™ LUBRICOMP™ YL003 compound | SABIC Innovative Plastics | TPEE | LNP™ LUBRICOMP™ |