TOTAL Polyethylene MDPE HR 515
| Category: | MDPE , Medium Density Polyethylene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polyethylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TntPfB_TOTAL-Polyethylene-MDPE-HR-515.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MDPE HR 515 is a medium density polyethylene produced by slurry loop process with hexene as co-monomer. It shows a broad molecular weight distribution ensuring outstanding processability. MDPE HR 515 is especially dedicated to high rigidity film applications, particularly in blend and/or coextrusion with LDPE and/or LLDPE. MDPE HR 515 is suited for many film applications, in the field of consumer, industrial, food or hygiene packaging. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.942 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.22 | g/10 min | ISO 1133 |
| 190°C/21.6 kg | 18 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 810 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 20 µm, blown film | 23.0 | MPa | ISO 527-3 |
| TD : Yield, 20 µm, blown film | 24.0 | MPa | ISO 527-3 |
| MD : Yield, 40 µm, blown film | 22.0 | MPa | ISO 527-3 |
| TD : Yield, 40 µm, blown film | 22.0 | MPa | ISO 527-3 |
| MD : Broken, 20 µm, blown film | 65.0 | MPa | ISO 527-3 |
| TD : Broken, 20 µm, blown film | 53.0 | MPa | ISO 527-3 |
| MD : Broken, 40 µm, blown film | 55.0 | MPa | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 51.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 20 µm, blown film | 450 | % | ISO 527-3 |
| TD : Broken, 20 µm, blown film | 540 | % | ISO 527-3 |
| MD : Broken, 40 µm, blown film | 580 | % | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 660 | % | ISO 527-3 |
| Dart Drop Impact | ISO 7765-1 | ||
| 20 µm, blown film | 150 | g | ISO 7765-1 |
| 40 µm, blown film | 190 | g | ISO 7765-1 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 124 | °C | ISO 306 |
| Melting Temperature (DSC) | 127 | °C | ISO 3146 |
| Additional Information |
|---|
| Elmendorf, ISO 6383-2, MD, Blown Film, 20 µm: 8 N/mmElmendorf, ISO 6383-2, TD, Blown Film, 20 µm: 130 N/mmElmendorf, ISO 6383-2, MD, Blown Film, 40 µm: 12 N/mmElmendorf, ISO 6383-2, TD, Blown Film, 40 µm: 150 N/mm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 190 - 220 | °C | |
| Cylinder Zone 2 Temp. | 190 - 220 | °C | |
| Cylinder Zone 3 Temp. | 190 - 220 | °C | |
| Cylinder Zone 4 Temp. | 190 - 220 | °C | |
| Cylinder Zone 5 Temp. | 190 - 220 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8200-80UV Clear 8385 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| EPO-TEK® H35-175MP | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| Kumho EPS SEPS N20 | Korea Kumho Petrochemical Co., Ltd. | PS (EPS) | Kumho EPS |
| Jiangsu Sinarise EX9024X | Jiangsu Sinarise New Material Technology Co., Ltd | TPE | Jiangsu Sinarise |
| Hostacom PPU X9067HS C12470 | LyondellBasell Industries | PP Copolymer | Hostacom |