SCHULAMID® 6 GF 30 FR 4
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Tnd2mA_SCHULAMID-6-GF-30-FR-4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% glass fibre reinforced flame-retardant halogenated Polyamide 6 grade; without PBDE |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.55 | -- | g/cm³ | ISO 1183/A |
| Viscosity Number | 145 | -- | cm³/g | ISO 307 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 200 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9500 | 6800 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 155 | 107 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.5 | 5.2 | % | ISO 527-2/1A/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 6.0 | -- | kJ/m² | |
| 23°C | 10 | 13 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 58 | -- | kJ/m² | |
| 23°C | 65 | 74 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 216 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 202 | -- | °C | ISO 75-2/Af |
| Ball Pressure Test (200°C) | Pass | -- | IEC 60695-10-2 | |
| RTI Elec | UL 746 | |||
| 0.750 mm | 65.0 | -- | °C | |
| 1.50 mm | 65.0 | -- | °C | |
| 3.00 mm | 65.0 | -- | °C | |
| RTI Imp | UL 746 | |||
| 0.750 mm | 65.0 | -- | °C | |
| 1.50 mm | 65.0 | -- | °C | |
| 3.00 mm | 65.0 | -- | °C | |
| RTI Str | UL 746 | |||
| 0.750 mm | 65.0 | -- | °C | |
| 1.50 mm | 65.0 | -- | °C | |
| 3.00 mm | 65.0 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | > 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+13 | > 1.0E+10 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 250 | -- | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | UL 746 | |||
| 0.750 mm | PLC 0 | -- | ||
| 1.50 mm | PLC 0 | -- | ||
| 3.00 mm | PLC 0 | -- | ||
| Hot-wire Ignition (HWI) | UL 746 | |||
| 0.750 mm | PLC 0 | -- | ||
| 1.50 mm | PLC 0 | -- | ||
| 3.00 mm | PLC 0 | -- |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | ISO 3795 | |||
| 0.750 mm, Self-Extinguishing | 0.0 | -- | mm/min | |
| 1.50 mm, Self-Extinguishing | 0.0 | -- | mm/min | |
| 3.00 mm, Self-Extinguishing | 0.0 | -- | mm/min | |
| Flame Rating | UL 94, IEC 60695-11-10, -20 | |||
| 0.750 mm | V-0 | -- | ||
| 1.50 mm | V-0 | -- | ||
| 3.00 mm | V-0 | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.750 mm | 960 | -- | °C | |
| 1.50 mm | 960 | -- | °C | |
| 3.00 mm | 960 | -- | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 0.750 mm | 825 | -- | °C | |
| 1.50 mm | 825 | -- | °C | |
| 3.00 mm | 825 | -- | °C | |
| Oxygen Index | 30 | -- | % | ISO 4589-2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2800B-50A HF | RTP Company | TPV | RTP |
| SCHULAMID® 6 HV 2 FR | A. Schulman Europe | Nylon 6 | SCHULAMID® |
| Sindustris PP GP3203Z | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| WELLAMID Nylon 6600 GV 50 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| Sylvin 8359-75 Grey 9491 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |