Order Products : sales@su-jiao.com
Celcon® GC25T
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celcon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TlSbhs_Celcon-GC25T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Celcon® GC25T is a 25% glass fiber coupled acetal copolymer grade. It offers higher strength than the standard Celcon GC25-A. Celcon GC25T is FDA approved. Celcon GC25T is also exceptionally resistant to fuel. It offers excellent resistance to transportation fuels especially oxygenated fuels. Chemical abbreviation according to ISO 1043-1: POM |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Multi-Point Data |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.58 | g/cm³ | ASTM D792 |
| -- | 1.57 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow | 0.40 | % | ASTM D955 |
| Transverse flow | 1.0 | % | ASTM D955 |
| Vertical flow direction | 0.80 | % | ISO 294-4 |
| Flow direction | 0.40 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.80 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8630 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Fracture, 23°C | 138 | MPa | ASTM D638 |
| Fracture | 129 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 8520 | MPa | ISO 178 |
| Flexural Stress (23°C) | 202 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 7.2 | kJ/m² | ISO 179/1eA |
| 23°C | 8.7 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 55 | kJ/m² | ISO 179/1eU |
| 23°C | 50 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 8.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 163 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 161 | °C | ISO 75-2/A |
| Melting Temperature 1 | 165 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 2.7E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.3E-4 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 170 - 180 | °C | |
| Middle Temperature | 180 - 190 | °C | |
| Front Temperature | 180 - 190 | °C | |
| Nozzle Temperature | 190 - 200 | °C | |
| Processing (Melt) Temp | 180 - 200 | °C | |
| Mold Temperature | 90.0 - 120 | °C | |
| Injection Pressure | 90.0 - 140 | MPa | |
| Injection Rate | Slow | ||
| Holding Pressure | 90.0 - 140 | MPa | |
| Back Pressure | 0.00 - 0.500 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 190 to 210°CZone 4 Temperature: 190 to 200°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PONYL 4002G25 | POLYROCKS CHEMICAL CO., LTD | Nylon 66 | PONYL |
| Starflam BFR552Y3 | Eurostar Engineering Plastics | Nylon 6 | Starflam |
| HOPELEX PCN-2003 | Lotte Chemical Corporation | PC | HOPELEX |
| Sarlink® TPE FM-2270 XRD1 (PRELIMINARY DATA) | Teknor Apex Company | TPE | Sarlink® TPE |
| MAXAMID™ EPDM036-BK | Pier One Polymers, Inc. | Nylon 6 | MAXAMID™ |