Generic PP, Unspecified
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TlH700_Generic-PP-Unspecified.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PP, Unspecified This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.793 - 1.14 | g/cm³ | ASTM D792 |
| 23°C | 0.800 - 1.12 | g/cm³ | ISO 1183 |
| -- | 903 | kg/m³ | ISO 1183 1 |
| -- | 0.897 - 0.916 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/2.16 kg | 0.10 - 33 | g/10 min | ASTM D1238 |
| 230°C/2.16 kg | 0.10 - 26 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) | |||
| 230°C/2.16 kg | 2.00 - 41.2 | cm³/10min | ISO 1133 |
| -- | 20.4 | cm³/10min | ISO 1133 2 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.75 - 2.0 | % | ASTM D955 |
| Transverse flow : 23°C | 0.71 - 3.0 | % | ASTM D955 |
| 23°C | 1.4E-3 - 2.4 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 1.0E-3 - 0.043 | % | ASTM D570 |
| 23°C, 24 hr | 0.027 - 0.10 | % | ISO 62 |
| Saturated, 23°C | 0.010 - 0.060 | % | ASTM D570 |
| Equilibrium, 23°C | 0.030 - 0.062 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 7.9E-3 - 0.012 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| 23°C | 74 - 106 | ASTM D785 | |
| 23°C | 74 - 110 | ISO 2039-2 | |
| Durometer Hardness | |||
| 23°C | 54 - 98 | ASTM D2240 | |
| 23°C | 48 - 100 | ISO 868 | |
| Ball Indentation Hardness | 28.0 - 37.3 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 896 - 2140 | MPa | ASTM D638 |
| 23°C | 825 - 1810 | MPa | ISO 527-2 |
| -- | 1230 | MPa | ISO 527-2 3 |
| Tensile Strength | |||
| Yield, 23°C | 15.7 - 39.1 | MPa | ASTM D638 |
| Yield, 23°C | 16.6 - 36.8 | MPa | ISO 527-2 |
| Yield | 25.7 | MPa | ISO 527-2 4 |
| Fracture, 23°C | 17.3 - 44.9 | MPa | ASTM D638 |
| Fracture, 23°C | 11.4 - 36.7 | MPa | ISO 527-2 |
| 23°C | 15.0 - 36.2 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 0.75 - 13 | % | ASTM D638 |
| Yield, 23°C | 1.8 - 17 | % | ISO 527-2 |
| Yield | 8.5 | % | ISO 527-2 5 |
| Fracture, 23°C | 2.0 - 520 | % | ASTM D638 |
| Fracture, 23°C | 1.0 - 400 | % | ISO 527-2 |
| Tensile Elongation at Break | 49 - 50 | % | ISO 527-2 6 |
| Apparent Bending Modulus (23°C) | 825 - 840 | MPa | ASTM D747 |
| Flexural Modulus | |||
| 23°C | 693 - 2330 | MPa | ASTM D790 |
| 23°C | 557 - 2300 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 23.8 - 48.4 | MPa | ASTM D790 |
| 23°C | 19.5 - 52.1 | MPa | ISO 178 |
| Yield, 23°C | 26.6 - 48.9 | MPa | ASTM D790 |
| Coefficient of Friction | 0.39 - 0.71 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 15 - 79000 | µm | |
| Tensile Strength | |||
| MD : Yield | 0.588 - 34.5 | MPa | ASTM D882 |
| TD : Yield | 1.37 - 27.5 | MPa | ASTM D882 |
| 23°C | 23.0 - 120 | MPa | ISO 527-3 |
| Tensile Elongation | |||
| MD : Fracture | 140 - 520 | % | ASTM D882 |
| TD : Fracture | 49 - 92 | % | ASTM D882 |
| Fracture, 23°C | 20 - 900 | % | ISO 527-3 |
| Seal Initiation Temperature | 102 - 122 | °C |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23°C | 1.3 - 14 | kJ/m² | ISO 179 |
| -30°C | 19.5 | kJ/m² | ISO 179/1eA 7 |
| 23°C | 4.57 | kJ/m² | ISO 179/1eA 8 |
| Charpy Unnotched Impact Strength | |||
| 23°C | 1.0 - 25 | kJ/m² | ISO 179 |
| -30°C | 101 | kJ/m² | ISO 179/1eU 9 |
| Notched Izod Impact | |||
| 23°C | 7.5 - 92 | J/m | ASTM D256 |
| 23°C | 2.0 - 12 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 6.0 - 860 | J/m | ASTM D256 |
| 23°C | 8.0 - 60 | kJ/m² | ISO 180 |
| Multi-Axial Instrumented Impact Energy (23°C) | 0.900 - 35.0 | J | ISO 6603-2 |
| Dart Drop Impact (23°C) | 0.366 - 16.3 | J | ASTM D3029 |
| Dart Drop Impact (23°C) | 0.452 - 21.5 | J | ASTM D5420 |
| Tensile notched impact strength (23°C) | 65.1 | kJ/m² | ISO 8256/1 10 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 77.5 - 145 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 74.8 - 116 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 47.1 - 67.7 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 42.2 - 91.8 | °C | ISO 75-2/A |
| 1.8 MPa | 54.2 | °C | ISO 75-2 11 |
| Vicat Softening Temperature | |||
| -- | 123 - 155 | °C | ASTM D1525 |
| -- | 93.8 - 156 | °C | ISO 306 |
| 50°C/h, B (50N) | 79.3 | °C | ISO 306 12 |
| Melting Temperature | |||
| -- | 141 - 182 | °C | |
| -- | 134 - 151 | °C | DSC |
| -- | 159 - 175 | °C | ISO 11357-3 |
| -- | 149 - 185 | °C | ASTM D3418 |
| -- | 130 - 166 | °C | ISO 3146 |
| -- 13 | 165 | °C | ISO 11357-3 14 |
| Linear thermal expansion coefficient | |||
| Flow | 5.4E-5 - 1.6E-4 | cm/cm/°C | ASTM D696 |
| Flow | 8.9E-5 - 1.5E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral | 6.4E-5 - 1.5E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity (23°C) | 0.12 - 0.62 | W/m/K | ASTM C177 |
| RTI Elec | 65.0 - 116 | °C | UL 746 |
| RTI Imp | 65.0 - 120 | °C | UL 746 |
| RTI | 65.0 - 121 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 1.0E+2 - 2.5E+15 | ohms | ASTM D257 |
| -- | 1.0E+2 - 1.0E+9 | ohms | ASTM D4496 |
| -- | 1.1E+2 - 1.0E+16 | ohms | IEC 60093 |
| -- | 1.0E+12 - 1.1E+14 | ohms | IEC 60093 15 |
| Volume Resistivity | |||
| 23°C | 5.0 - 2.5E+16 | ohms·cm | ASTM D257 |
| 23°C | 1.0E+3 - 5.8E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| 23°C | 18 - 20 | kV/mm | ASTM D149 |
| 23°C | 19 - 43 | kV/mm | IEC 60243-1 |
| -- | 49 | kV/mm | IEC 60243-1 16 |
| Dielectric Constant | |||
| 23°C | 2.29 - 2.31 | ASTM D150 | |
| 23°C | 2.30 | IEC 60250 | |
| 100 Hz | 2.25 | IEC 60250 17 | |
| 1 MHz | 2.05 | IEC 60250 18 | |
| Dissipation Factor | |||
| 23°C | 2.0E-4 - 3.1E-3 | ASTM D150 | |
| 23°C | 1.0E-3 - 3.0E-3 | IEC 60250 | |
| 100 Hz | 8.1E-4 | IEC 60250 19 | |
| 1 MHz | 5.2E-3 | IEC 60250 20 | |
| Arc Resistance | 76.0 - 137 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 600 | V | UL 746 |
| Comparative Tracking Index | 450 - 600 | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | 196 - 200 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | 0.00 - 0.324 | mm/min | UL 746 |
| Hot-wire Ignition (HWI) | 6.0 - 56 | sec | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index | 849 - 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 743 - 960 | °C | IEC 60695-2-13 |
| Oxygen Index | |||
| -- | 27 - 34 | % | ASTM D2863 |
| -- | 23 - 28 | % | ISO 4589-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | 46 - 136 | ASTM D2457 | |
| Haze | 0.30 - 80 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 69.6 - 93.6 | °C | |
| Drying Time | 1.9 - 4.0 | hr | |
| Suggested Max Moisture | 9.4E-3 - 0.050 | % | |
| Suggested Max Regrind | 15 | % | |
| Rear Temperature | 160 - 248 | °C | |
| Middle Temperature | 179 - 222 | °C | |
| Front Temperature | 189 - 248 | °C | |
| Nozzle Temperature | 195 - 246 | °C | |
| Processing (Melt) Temp | 190 - 231 | °C | |
| Mold Temperature | 30.0 - 65.0 | °C | |
| Injection Pressure | 56.9 - 86.3 | MPa | |
| Holding Pressure | 4.48 - 78.5 | MPa | |
| Back Pressure | 0.175 - 1.27 | MPa | |
| Screw Speed | 44 - 80 | rpm | |
| Cushion | 7.50 - 15.0 | mm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PP, UnspecifiedThis information is provided for comparative purposes only. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 69.6 - 91.1 | °C | |
| Drying Time | 1.5 - 3.1 | hr | |
| Cylinder Zone 1 Temp. | 159 - 231 | °C | |
| Cylinder Zone 2 Temp. | 170 - 260 | °C | |
| Cylinder Zone 3 Temp. | 168 - 280 | °C | |
| Cylinder Zone 4 Temp. | 170 - 241 | °C | |
| Cylinder Zone 5 Temp. | 170 - 313 | °C | |
| Adapter Temperature | 197 - 238 | °C | |
| Melt Temperature | 208 - 260 | °C | |
| Die Temperature | 199 - 310 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PP, UnspecifiedThis information is provided for comparative purposes only. |
| Note Message | |
|---|---|
| 1 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 2 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 3 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 4 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 5 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 6 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 7 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 8 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 9 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 10 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 11 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 12 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 13 . | 10 °C/min |
| 14 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 15 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 16 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 17 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 18 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 19 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 20 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenac™ LA543 | Asahi Kasei Chemicals Corporation | Acetal (POM) Homopolymer | Tenac™ |
| Starglas FX05032 | Eurostar Engineering Plastics | PE, Unspecified | Starglas |
| MTM® 28 series | Cytec Industries Inc. | Epoxy | MTM® |
| Verolloy D200 | PlastxWorld Inc. | PC Alloy | Verolloy |
| GAPEX® FPP30GQ04 BLACK | Ferro Corporation | PP, Unspecified | GAPEX® |