POLYNIL® C3588
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Nilit Plastics |
| Trademark: | POLYNIL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Tku43b_POLYNIL-C3588.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
POLYNIL® C3588 is an unreiforced Polyamide 66/6 (Nylon 66/6) high flow copolymer for compounding and alloying. This general pourpose 2.4 viscosity Polyamide 66/6 resin is FDA compliant. |
| General Information | |
|---|---|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.13 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 1.5 | % | |
| Saturation, 23°C | 8.5 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2.50 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 81.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 80 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2500 | MPa | ISO 178 |
| Flexural Stress (23°C) | 110 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 5.5 | kJ/m² | |
| 23°C | 6.5 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact Strength (23°C) | 6.0 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 210 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 65.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 220 | °C | ISO 306/B |
| Ball Pressure Test | IEC 60695-10-2 | ||
| 125°C | Pass | ||
| 165°C | Pass | ||
| Melting Temperature | 249 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (3.20 mm, Solution A) | 600 | V | IEC 60112 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALLOY® A1610 | Mitsubishi Chemical Performance Polymers, Inc. | TPE | PRIMALLOY® |
| Mowiol® 40-88 | Kuraray Co., Ltd. | PVOH | Mowiol® |
| GAPEX® RPP30EB80HB NATURAL | Ferro Corporation | PP Homopolymer | GAPEX® |
| Hangzhou Jinxin VMBOPP Film | Hangzhou Jinxin Filming Packaging Co., Ltd. | Film, BOPP | Hangzhou Jinxin |
| SEQUEL® 1480 PUV NATRL | LyondellBasell Industries | TPO (POE) | SEQUEL® |