MAJ'ECO GP264M
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJ'ECO |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TkZEIW_MAJ-ECO-GP264M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAJ'ECO GP264M is a high flow vegetal fibre polypropylene compound intended for injection moulding. MAJ'ECO GP264M has been developed especially for demanding applications in various engineering sectors. APPLICATIONS Product such as:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.980 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 30 | g/10 min | ISO 1133 |
| Molding Shrinkage (2.00 mm) | 1.1 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2700 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 30.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 3.5 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 2450 | MPa | ISO 178 |
| Flexural Stress (23°C) | 82.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.1 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 21 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 148 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 91.0 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 150 - 190 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROMID A 260 Y0 | Taro Plast S.p.A. | Nylon 66/6 | TAROMID A |
| Unipren® Elastomers A3 PRTA010 45A UP304 | Petropol Industry and Trade of Polymers LTDA | SEBS | Unipren® Elastomers |
| ZELAS® MC721AP | Mitsubishi Chemical Performance Polymers, Inc. | TPE | ZELAS® |
| CGPC PVC H-58 | China General Plastics Corporation | PVC, Unspecified | CGPC PVC |
| LNP™ LUBRICOMP™ EFL36 compound | SABIC Innovative Plastics | PEI | LNP™ LUBRICOMP™ |