KRATON® D1160 B
| Category: | SIS , Styrene Isoprene Styrene Block Copolymer |
| Manufacturer: | Kraton Polymers LLC |
| Trademark: | KRATON® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TkDfoK_KRATON-D1160-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Kraton D1160 B is a clear linear triblock copolymer based on styrene and isoprene with bound styrene of 18.5% mass. It is supplied from South America in the physical form identified below:
Kraton D1160 BT is used in formulating adhesives, in particular hot melt pressure sensitive adhesives. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ISO 2781 |
| Apparent Density 1 | 0.35 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 5.0 to 13 | g/10 min | ISO 1133 |
| Solution Viscosity 2 | 700 to 1100 | mPa·s | Internal Method |
| Antioxidant Additive | > 0.080 | % | Internal Method |
| Ash Content - Product Form "BT" | < 0.50 | % | ISO 247-B |
| Extractables | < 1.0 | % | Internal Method |
| Molecular Weight | 168000 to 188000 | g/mol | Internal Method |
| Polystyrene Content | 17 to 21 | % | Internal Method |
| Volatile Matter | < 0.30 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A, 30 sec, Compression Molded) | 48 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 3(300% Strain) | 1.90 | MPa | ISO 37 |
| Tensile Stress 4(Yield) | 32.0 | MPa | ISO 37 |
| Tensile Elongation 5(Break) | 1300 | % | ISO 37 |
| Note Message | |
|---|---|
| 1 . | Method B |
| 2 . | Measured on 25% mass solution in toluene at 25°C using a Brookfield viscometer, LTF or LTV model |
| 3 . | Measured on films cast from a solution in toluene |
| 4 . | Measured on films cast from a solution in toluene |
| 5 . | Measured on films cast from a solution in toluene |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Roechling Matrox® | Röchling Engineering Plastics SE & Co. KG | UHMWPE | Roechling |
| Silmar® SIL93BE-956 | Interplastic Corporation | Polyester, TS | Silmar® |
| VITAMIDE® AR36NT8506 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| Clariant Nylon 6 PA-211 | Clariant Corporation | Nylon 6 | Clariant Nylon 6 |
| Kuraray Poval® PVA 205MB | Kuraray Co., Ltd. | PVOH | Kuraray Poval® |