Self-lubricating product based on Polyetheretherketone (PEEK). PTFE. Carbon fibre. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.47 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.35 to 0.55 | % | |
| Flow : 2.00 mm | 0.10 to 0.30 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 22500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 170 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 1.0 | % | ISO 527-2/5 |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic | 0.24 | ||
| vs. Itself - Static | 0.30 | ||
| Wear Factor | 60 | 10^-8 mm³/N·m | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 25 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 350 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 350 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 350 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 150 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 370 to 400 | °C | |
| Mold Temperature | 170 to 200 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 60 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E Wire & Cable GA-1046-80E | S&E Specialty Polymers, LLC | PVC, Semi-Rigid | S&E Wire & Cable |
| Unipren® Elastomers A3 NTLA010 70A UP303 | Petropol Industry and Trade of Polymers LTDA | SEBS | Unipren® Elastomers |
| Aegis® H95ZI | Honeywell | Nylon 6 | Aegis® |
| Badamid® PA12 GF30 | Bada AG | Nylon 12 | Badamid® |
| Karina GREEN COLOCOR CONCENTRATE 40/ 21-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |