OnFlex™ AF 7210-60
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | PolyOne Corporation |
| Trademark: | OnFlex™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Th0dlH_OnFlexAF721060.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Onflex™AF 7210-60 is an easy-to-process TPE, mainly developed for various applications of automobiles.
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 0.990 | g/cm³ | ISO 1133, ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| Shao A, 3 seconds 2 | 60 | ISO 868 | |
| Shaw A, 10 seconds 3 | 57 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Fracture 4 | 8.50 | MPa | ISO 37 |
| Fracture 5 | 7.50 | MPa | ASTM D412 |
| Tensile Elongation | |||
| Fracture 6 | 750 | % | ISO 37 |
| Fracture 7 | 700 | % | ASTM D412 |
| Tear Strength | |||
| -- 8 | 31.0 | kN/m | ISO 34-1 |
| -- 9 | 27.5 | kN/m | ASTM D624 |
| Compression Set | |||
| 23°C, 72 hr 10 | 27 | % | ISO 815 |
| 23°C, 72 hr 11 | 26 | % | ASTM D395 |
| 70°C, 22 hr 12 | 39 | % | ISO 815 |
| 70°C, 22 hr 13 | 42 | % | ASTM D395 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | DIN 75200 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Weather Resistance - (1500h) | passed (black version) | SAE J2527 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 160 - 188 | °C | |
| Middle Temperature | 177 - 193 | °C | |
| Front Temperature | 188 - 210 | °C | |
| Nozzle Temperature | 188 - 216 | °C | |
| Mold Temperature | 30 - 60 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.00 - 0.827 | MPa | |
| Screw Speed | 40 - 100 | rpm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 - 220 | °C |
| Note Message | |
|---|---|
| 1 . | 2 hours |
| 2 . | 2 hours |
| 3 . | China |
| 4 . | 2 hours |
| 5 . | China |
| 6 . | 2 hours |
| 7 . | China |
| 8 . | 2 hours |
| 9 . | China |
| 10 . | 2 hours |
| 11 . | China |
| 12 . | 2 hours |
| 13 . | China |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Trexprene® A64CI | Mitsubishi Chemical Performance Polymers, Inc. | TPV | Trexprene® |
| Vydyne® R530HR BK652 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| APEX® 81-D322-D | Teknor Apex Company | PVC, Flexible | APEX® |
| Sylvin 5175-92 White 1478 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| POCAN® S 1517 000000 | LANXESS GmbH | PBT | POCAN® |