Ultramid® A3EG3 BK00564
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Tdkg8g_Ultramid-A3EG3-BK00564.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid A3EG3 BK00564 is a 15% glass fiber reinforced, pigmented black, injection molding PA66 grade. Applications Typical applications include medium stiffness machinery components and housings, as well as electrically insulating parts. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 7.0 | % | |
| Equilibrium, 23°C, 50% RH | 2.2 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 6000 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 122 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.5 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.5 | kJ/m² | ISO 179 |
| Notched Izod Impact Strength (23°C) | 5.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 246 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 260 | °C | ISO 3146 |
| CLTE | |||
| Flow | 3.3E-5 | cm/cm/°C | |
| Transverse | 7.5E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 280 to 305 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Scolefin 34 G 10-9 | Ravago Group | PP Homopolymer | Scolefin |
| Bynel® E418 | DuPont Packaging & Industrial Polymers | EVA | Bynel® |
| EnCom PC-PBT 1013 | EnCom, Inc. | PC+PBT | EnCom |
| Lumid® HI1102A(W) | LG Chem Ltd. | Nylon 6 | Lumid® |
| LNP™ THERMOCOMP™ PF00ASXS compound | SABIC Innovative Plastics | Nylon 6 | LNP™ THERMOCOMP™ |