LNP™ LUBRICOMP™ CBL36XXC compound
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TcEYrg_LNPLUBRICOMPCBL36XXCcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP CBL36XXC is a compound based on Polystyrene resin containing Glass Bead, PTFE. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound CBL-4036 Product reorder name: CBL36XXC |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (24 hr) | 0.50 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 5560 | MPa | ASTM D638 |
| Tensile Strength (Break) | 22.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus | 4080 | MPa | ASTM D790 |
| Flexural Strength | 41.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 11 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 77 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 77.8 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VORAZ™ 511 | Greene, Tweed & Co. | Perfluoroelastomer | VORAZ™ |
| HiFill® PA6 GF15 HS L | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| Hoffman PVC V4-220 | Hoffman Plastic Compounds Inc. | PVC, Flexible | Hoffman PVC |
| Hostacom TKC 2007N | LyondellBasell Industries | PP Copolymer | Hostacom |
| WELLAMID Nylon 6000 MRCF 15/15 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |