Order Products : sales@su-jiao.com
Pro-fax 6523
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Pro-fax |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TbsRnY_Pro-fax-6523.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Pro-fax 6523 general purpose polypropylene homopolymer resin is available in pellet form. An ASTM and ISO-based versions of the technical datasheet are available for Pro-fax 6523. For regulatory compliance information see Pro-fax 6523 Product Stewardship Bulletin (PSB). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.898 | g/cm³ | ASTM D792B |
| -- | 0.900 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 33.0 | MPa | ASTM D638 |
| Yield, 23°C | 30.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 12 | % | ASTM D638 |
| Yield, 23°C | 12 | % | ISO 527-2 |
| Flexural Modulus | |||
| 1% Secant 2 | 1380 | MPa | ASTM D790A |
| 23°C | 1270 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.7 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 53 | J/m | ASTM D256A |
| 23°C | 6.2 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 88.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 79.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 50.0 | °C | ISO 75-2/A |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Regis® 6225 | Noble Polymers | Polyolefin, Unspecified | Regis® |
| UBE Nylon 5033 TX7 | UBE Engineering Plastics, S.A. | Nylon 66/6 | UBE Nylon |
| ALTECH® ABS A 1000/106 | ALBIS PLASTIC GmbH | ABS | ALTECH® ABS |
| DINALON® PA 6 IGNÍFUGA 30% FV | Grupo Repol | Nylon 6 | DINALON® |
| Ecollent™ PC/ABS | Lucent Polymers, Inc. | PC+ABS | Ecollent™ |