Radilon® A 24EPT3010UK 333 NER
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Radici Plastics |
| Trademark: | Radilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Tbc5BX_Radilon-A-24EPT3010UK-333-NER.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PA66 low viscosity injection moulding grade. Toughened and plasticized. Improved UV resistance. Natural colour. Suitable for parts requiring high productivity like fasteners, connectors, cable ties. ISO 1043 : PA66-HITP |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.09 | -- | g/cm³ | ISO 1183 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 1150 | -- | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 40.0 | -- | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 25 | -- | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | > 100 | -- | % | ISO 527-2/1A/50 |
| Flexural Modulus 1 | 950 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 33.0 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 80 | -- | kJ/m² | ISO 179/1eA |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 50.0 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 120 | -- | °C | ISO 306/B50 |
| Melting Temperature 3 | 255 | -- | °C | ISO 11357 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | < 30 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 80.0 | °C | |
| Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr | |
| Dew Point - Desiccant Dryer | < -20.0 | °C | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C | |
| Injection Rate | Moderate |
| Extrusion | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Melt Temperature | 270 to 290 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris ABS LER572 | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| Staramide AG4 | Eurostar Engineering Plastics | Nylon 66 | Staramide |
| TARODUR 100 G3 | Taro Plast S.p.A. | ABS | TARODUR |
| Daelim Po1y® LH-418S | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| POLYCOMPO PE 403P | POLYCOMPO Co.,Ltd. | LDPE | POLYCOMPO PE |