LNP™ THERMOCOMP™ DX14354X compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TbHh5w_LNP-THERMOCOMP-DX14354X-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP Thermocomp compound DX14354X is an improved flow, colorable compound based on PC copolymer resin developed for applications that require Laser Direct Structuring (LDS) for antenna, or electronic circuit manufacturing. Thermocomp compound DX14354X helps customers to improve productivity with stable plating and RF performance, excellent impact strength and surface finish. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.29 | g/cm³ | ASTM D792 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 260°C/5.0 kg | 25.0 | cm³/10min | |
| 280°C/2.16 kg | 27.0 | cm³/10min | |
| 280°C/21.6 kg | 22.0 | cm³/10min | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.50 to 0.70 | % | |
| Across Flow : 24 hr | 0.50 to 0.70 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.050 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2500 | MPa | ASTM D638 |
| -- | 2460 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 54.0 | MPa | ASTM D638 |
| Yield | 54.0 | MPa | ISO 527-2/50 |
| Break 3 | 49.0 | MPa | ASTM D638 |
| Break | 47.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 5.0 | % | ASTM D638 |
| Yield | 5.0 | % | ISO 527-2/50 |
| Break 5 | 70 | % | ASTM D638 |
| Break | 80 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2500 | MPa | ASTM D790 |
| -- 7 | 2560 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 86.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 85.0 | MPa | ASTM D790 |
| Break, 50.0 mm Span 9 | 83.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 750 | J/m | ASTM D256 |
| 23°C 10 | 60 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 111 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 113 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 128 | °C | ASTM D1525 12 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 5.7E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 6.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.2E+16 | ohms | ASTM D257 |
| Volume Resistivity | 1.2E+16 | ohms·cm | ASTM D257 |
| Dielectric Constant | |||
| 1.00 GHz | 3.10 | ASTM D150 | |
| 1.10 GHz | 3.06 | Internal Method | |
| 1.90 GHz | 3.08 | Internal Method | |
| 5.00 GHz | 3.08 | Internal Method | |
| Dissipation Factor | |||
| 1.00 GHz | 6.0E-3 | ASTM D150 | |
| 1.10 GHz | 6.3E-3 | Internal Method | |
| 1.90 GHz | 6.1E-3 | Internal Method | |
| 5.00 GHz | 5.9E-3 | Internal Method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.00 mm) | V-1 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 40.0 to 60.0 | °C | |
| Rear Temperature | 230 to 245 | °C | |
| Middle Temperature | 240 to 255 | °C | |
| Front Temperature | 245 to 265 | °C | |
| Nozzle Temperature | 240 to 260 | °C | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 40.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*3 |
| 11 . | 80*10*4 mm |
| 12 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LDPE 2801H0W | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| Vydyne® R533H NAT | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| VAMPLEN 1025 V2 | Vamp Tech | PP Homopolymer | VAMPLEN |
| Achieve™ 6936G2 | ExxonMobil Chemical | PP Homopolymer | Achieve™ |
| KumhoSunny PBT 3710FG | Shanghai KumhoSunny Plastics Co., Ltd. | PBT | KumhoSunny PBT |