Iupiace® TX903B
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Iupiace® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TbEoZ2_Iupiace-TX903B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Iupiace® TX903B is a Polyphenylene Ether + PS (PPE+PS) material filled with filler. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Iupiace® TX903B are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.09 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/2.16 kg) | 2.50 | cm³/10min | ISO 1133 |
| Water Absorption (Saturation, 23°C) | 0.060 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2700 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 60.0 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 40 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2700 | MPa | ISO 178 |
| Flexural Stress (23°C) | 100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 32 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 145 | °C | ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 250 to 280 | °C | |
| Middle Temperature | 270 to 300 | °C | |
| Front Temperature | 270 to 300 | °C | |
| Nozzle Temperature | 270 to 300 | °C | |
| Mold Temperature | 80.0 to 110 | °C | |
| Injection Pressure | 20.0 to 150 | MPa | |
| Injection Rate | Moderate | ||
| Screw Speed | 60 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 6168-89 Natural | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| GLAMIDE® T-422VOR | TOYOBO America, Inc. | Nylon 6 | GLAMIDE® |
| HiFill® PA6/6 LGF60 HS L UV 12mm | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| KOPA® KN333G20BL | Kolon Plastics, Inc. | Nylon 66 | KOPA® |
| Karina BLUE COLOR CONCENTRATE -E 06/256-GI | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |