TECHNYL® A 216 NATURAL FA
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TZWl3R_TECHNYL-A-216-NATURAL-FA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unreinforced polyamide 66, medium viscosity, for injection moulding. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.14 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 1.9 | -- | % | |
| Flow | 1.9 | -- | % | |
| Water Absorption (23°C, 24 hr) | 1.3 | -- | % | ISO 62 |
| Molding Shrinkage Isotropy | 1.00 | -- | Internal Method |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3000 | 1500 | MPa | ISO 527-2/1A |
| Tensile Stress | ISO 527-2/1A | |||
| Yield | 81.0 | 60.0 | MPa | |
| Break | 80.0 | 65.0 | MPa | |
| Tensile Strain | ISO 527-2/1A | |||
| Yield | 4.2 | 30 | % | |
| Break | 30 | 300 | % | |
| Flexural Modulus | 2900 | 1300 | MPa | ISO 178 |
| Flexural Stress | 120 | 50.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 4.5 | 14 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | No Break | No Break | ISO 179/1eU | |
| Notched Izod Impact Strength | 4.0 | 12 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 75.0 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 263 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 85°C | 2.5E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 85°C | 7.0E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+15 | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 4.0E+15 | 1.0E+14 | ohms·cm | IEC 60093 |
| Electric Strength | 30 | 26 | kV/mm | IEC 60243-1 |
| Relative Permittivity | 2.90 | 3.20 | IEC 60250 | |
| Dissipation Factor | 0.030 | 0.080 | IEC 60250 | |
| Comparative Tracking Index | IEC 60112 | |||
| Solution A | 600 | 575 | V | |
| Solution B | 525 | -- | V |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | V-2 | -- | ||
| 1.60 mm | V-2 | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.800 mm | 650 | -- | °C | |
| 1.60 mm | 650 | -- | °C | |
| Glow Wire Ignition Temperature (1.60 mm) | 650 | -- | °C | IEC 60695-2-13 |
| Oxygen Index | 27 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 270 to 275 | °C | |
| Middle Temperature | 280 to 285 | °C | |
| Front Temperature | 285 to 290 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Borealis PP BC545MO | Borealis AG | PP Impact Copolymer | Borealis PP |
| Dryflex® A2 660501 | ELASTO | SEBS | Dryflex® |
| EcoLon® MR1660-BK1 | Wellman Engineering Resins | Nylon 66 | EcoLon® |
| Geon™ Vinyl Flexible XV3772 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| LEXAN™ LUX7636C resin | SABIC Innovative Plastics | PC | LEXAN™ |